• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.658-659
• /
• 2006

Magnetron sputtered TiN, (Ti, Al)N and TiN/(Ti, Al)N multilayer coatings grown on cemented carbide substrates have been characterized by using electron probe microanalysis (EPMA), X-ray diffraction (XRD), scanning electron spectroscopy (SEM), nanoindentation, scratcher and cutting tests. Results show that TiN coating is bell mouth columnar structures, (Ti, Al)N coating is straight columnar structures and the modulation structure has been formed in the TiN/(Ti, Al)N multilayer coating. TiN/(Ti, Al)N multilayer coating exhibited higher hardness, better adhesion with substrate and excellent cutting performance compared with TiN and (Ti, Al)N coating.

• 한국표면공학회지
• /
• 제29권4호
• /
• pp.261-267
• /
• 1996

The characteristics and adhesion strength of TiN layer deposited by D. C. magnetron sputtering were investigated. Three types of TiN layers were deposited on STS304 stainless steel. Scratch tests were performed to determine the effect of deposition temperature, the thickness of coated TiN layer and the titanium inter-layer on the adhesion strength. TiN multilayer with titanium inter-layer showed the highest critical load in the deposition temperature range of $25^{\circ}C$ to $300^{\circ}C$. Adhesion strength of TiN multilayer with titanium inter-layer was raised from 15N to 20N by raising deposition temperature from $25^{\circ}C$ to $400^{\circ}C$. Adhesion strength was raised from 18N to 38N by increasing the thickness of outer layer of TiN multilayer from 2.1 $\mu\textrm{m}$ to 9.5 $\mu\textrm{m}$.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 하계학술대회 논문집
• /
• pp.19-19
• /
• 2009

TiNxOy/TiNx multilayer thin films with a high resistance (~ k$Omega$) were deposited on SiO2/Si substrates at room temperature by sputtering. The TiNx thin films show island and smooth surface morphology in samples prepared by dc and rf magnetron sputtering, respectively. TiNxOy/TiNx multilayer has been developed to control temperature coefficient of resistance (TCR) by the incorporation of TiNx layer (positive TCR) inserted into TiNxOy layers(negative TCR). Electrical and structural properties of sputtered TiNxOy/TiNx multilayer films were investigated as a function of annealing temperature. In order to achieve a stable high resistivity, multilayer films were annealed at various temperatures in oxygen ambient. Samples annealed at 700 oC for 1 min exhibit a good TCR value and a stable high resistivity.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 1998년도 춘계학술발표회 초록집
• /
• pp.17-17
• /
• 1998

• 한국세라믹학회지
• /
• 제56권1호
• /
• pp.49-55
• /
• 2019

$Ti_{0.33}Al_{0.67}N/CrN$ nano-multilayers, which are known to have excellent wear resistance, were prepared using an unbalanced magnetron sputter to have various periods of 2-5 nm. $Ti_{0.33}Al_{0.67}N$ had a hexagonal structure in a single layer, but converted to a cubic structure by forming a multilayer with CrN, which has a cubic structure. Thus, $Ti_{0.33}Al_{0.67}N$ formed a superlattice in the multilayer. The $Ti_{0.33}Al_{0.67}/CrN$ multilayer with a period of 2.5 nm greatly exceeded the hardness of the $Ti_{0.33}Al_{0.67}N$ and the CrN single layer, reaching 39 GPa. According to the low angle X-ray diffraction results, the $Ti_{0.33}Al_{0.67}N/CrN$ multilayer maintained its as-coated structure to a temperature as high as $700^{\circ}C$ and exhibited hardness of 30 GPa. The thickness of the oxide layer of the $Ti_{0.33}Al_{0.67}N/CrN$ multilayered coating was less than one-tenth of those of the single layers. Thus, $Ti_{0.33}Al_{0.67}N/CrN$ multilayered coating had hardness and oxidation resistance far superior to those of its constituent single layers.

• 한국재료학회지
• /
• 제1권1호
• /
• pp.9-17
• /
• 1991

화학증착법에 의해 $Si_3N_4-TiC$ 복합재료 위에 코팅된 TiC 박막은 TiN 박막에 비하여 우수한 미세구조와 열충격저항, 계면결합을 가지고 있는 것으로 나타났다. 화학증착법에 의한 TiN 박막은 TiC 박막에 비해 강철과의 마찰계수가 작고 화학적으로 안정하였다. 실험결과는 코팅된 절삭공구가 우수한 내 마모성을 갖고 있는 것으로 나타났다. 또한, 다중 코팅된 절삭공구는 단일 코팅된 공구보다 우수한 내 마모성을 보였다

• 한국표면공학회지
• /
• 제42권4호
• /
• pp.161-168
• /
• 2009

Effects of TiN/Ti multilayer coating on the Ti-30Ta-xZr alloy surface were studied by using various experiments. The Ti-30Ta containing Zr (5, 10 and 15 wt%) were melted 10 times to improve chemical homogeneity by using a vacuum furnace. And then samples were homogenized for 24 hrs at $1000^{\circ}C$. The specimens were prepared for TiN/Ti coating by cutting and polishing. The prepared specimens were coated with TiN/Ti multilayers by using DC magnetron sputtering method. The analyses of coated surface and coated layer were carried out by field emission scanning electron microscope(FE-SEM), EDX, and X-ray diffractometer(XRD). From the microstructure and XRD analysis of Ti-30Ta-xZr alloys, The equiaxed structure was changed to needle-like structure with increasing Zr content. And $\alpha$-peak and elastic modulus increased as Zr content increased. The $\alpha$ and $\beta$ phase predominantly were found in the specimen containing high Zr content. According to the analysis of TiN/Ti coating layer, the surface defects and structures of Ti-30Ta-xZr were covered with TiN/Ti coating layer and surface roughness decreased.

• 한국산학기술학회논문지
• /
• 제15권3호
• /
• pp.1253-1258
• /
• 2014

CA 이온도금기술에 의한 TiC와 TiN 그리고 TiC/TiN 코팅재를 비교하기 위하여 트라이볼로지 물성을 연구하였다. 실험은 Falex journal V block 시스템을 이용한 터보시험기에서 수행하였다. 코팅재의 마찰과 마모특성은 작용된 하중과 미끄럼 속도에 의하여 다양하게 결정되었다. TiC와 TiN 그리고 TiC/TiN 코팅재는 표면에서 트라이볼로지 특성이 현저하게 증가하였다. 단층코팅에서는 TiC보다 TiN이 좋은 결과를 얻었다. 그러나, TiC/TiN의 다층코팅은 다른 어떤 단층코팅보다 좋은 성능을 보였다. 다층코팅의 성능이 향상된 핵심요소는 TiN층 외부와 강 사이에서 부착이 증가하게된 TiC의 역할 때문이다.

• 한국재료학회지
• /
• 제28권7호
• /
• pp.405-410
• /
• 2018

TiN and CrN thin films are among the most used coatings in machine and tool steels. TiN and CrN are deposited by arc ion plating(AIP) method. The AIP method inhibits the reaction by depositing a hard, protective coating on the material surface. In this study, the characteristics of multi-layer(TiN/CrN/TiN(TCT), CrN/TiN/CrN(CTC)) are investigated. For comparison, TiN with the same thickness as the multilayer is formed as a single layer and analyzed. Thin films formed as multilayers are well stacked. The characteristics of micro hardness and corrosion resistance are better than those of single layer TiN. The TiN/CrN peak is confirmed because both TCT and CTC are formed of the same component(TiN, CrN), and the phase is first grown in the (111) direction, which is the growth direction. However, the adhesion and abrasion resistance of the multilayer films are somewhat lower.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2008년도 추계학술대회 초록집
• /
• pp.64-65
• /
• 2008

본 연구에서는 임상적으로 사용후 파절된 Ni-Ti파일의 표면 거동을 조사해보고 피로파괴수명 연장을 위하여 표면에 TiN/Ti 및 ZrN/Ti를 다층막으로 코팅한 후 표면의 특성을 조사하였다.