Abstract
The analysis of the effect of loading on chloride penetration into concrete is very important. In this study, we confirmed that the chloride penetration rates for plain and BFS concrete were increased by 47% and 89% under compressive stress, respectively. The diffusion coefficient of BFS concrete was lower than for conventional concrete with no BFS, no loads, and under stressed states. Therefore, BFS substitution plays an important role in the repression of chloride penetration even under compressive stress. Under compressive stress,the diffusion coefficient for BFS concrete was higher with increasing stress, and this was also the case for plain concrete. However, BFS concrete was strongly influenced by compressive stress in comparison to plain concrete. We investigated the effect of the difference of specific surfaces on the diffusion coefficient. As a result, the larger specific surface of BFS exhibited a lower diffusion coefficient. This tendency was most pronounced under the high stress conditions.
하중을 고려한 염분침투성의 평가가 대단히 중요한 것으로 확인되었다. 본 연구에서는 압축응력하에서 Plain콘크리트에서는 47%정도, BFS콘크리트에서는 89%정도 증가 하는 것으로 나타났다. 무하중 상태에서 BFS를 혼입한 콘크리트의 확산계수가 BFS 무혼입 콘크리트에 비해 적은 것이 확인되었다. 이러한 영향은 압축응력이 발생하는 환경하에서도 같은 경향을 나타내었다. 압축응력이 작용하는 환경 하에서 BFS콘크리트는 Plain콘크리트와 같이 하중의 증가와 함께 확산계수가 증가하는 것으로 확인 되었다. 또한, Plain콘크리트에 비해 압축하중의 영향을 크게 받는 것으로 확인 되었다. BFS의 비표면적이 높을수록 확산 계수가 작은 것으로 확인되었고, 이러한 경향은 고응력 환경에서 현저히 나타나는 것이 확인되었다. BFS의 치환율이 증가할수록 확산계수가 작은 것이 확인되었다. 또한, 압축응력이 작용하는 환경 하에서 BFS의 치환에 의한 염분침투성의 억제 효과가 더욱 더 현저히 나타나는 것으로 확인되었다.