Lifetime Prediction of Acrylic Resin for Metal Artifacts Reinforcement

금속유물 강화용 아크릴수지 수명예측

  • Gwak, Hongin (Conservation Science Lab., JinJu National Museum) ;
  • Kim, Jinkuk (Department of Polymer Science and Engineering, Gyeongsang National University)
  • 곽홍인 (국립진주박물관 보존과학실) ;
  • 김진국 (경상대학교 고분자공학과)
  • Published : 2009.12.01
Download PDF
⟨ Previous Next ⟩

Abstract

The purpose of this study is to determine the lifetime of acrylic resin ParaloidTM B-72(EMA copolymer), which is widely used as a coating for metallic artifacts to prevent corrosion. Lifetime factor with temperature, selected chromaticity as the test parameter for lifetime prediction. The found result is that the temperature is the most crucial factor influencing the prediction of the lifetime of the EMA copolymer coated iron surface against corrosion. The simulation results, based on Arrhenius Equation, showed that the lifetime prediction of the EMA coated iron surface was 24.5 years at 16℃, 17.1 years at 20℃, and 12.0 years at 24℃, respectively.

금속유물 강화제로 널리 사용 중인 아크릴계 수지 ParaloidTM B-72(EMA copolymer)의 수명예측을 위한 연구이다. 수명인자로서는 온도를 고려하였으며, 수명예측을 위한 test parameter로써 색도를 선택하였다. 그 결과, 같은 농도의 도막에서 온도에 대한 노화가 주요 요인이라는 것을 알았다. 즉 환경온도 24℃에서 24시간일 때 수명은 12.0년, 20℃에서 24시간일 때 수명은 17.1년, 16℃에서 24시간일 때 수명은 24.5년으로 예측되었다. 이 실험을 평가는 Arrhenius 관계식을 이용하여 예측하였다.