(Department of Forest Products, Chungnam National University)
;
This research was carried out to use green tea leaves powder for scavenging effects of volatile organic compounds on the UV varnishes and adhesives of fancy cherry veneer overlaid on the PF resin bonded Meranti plywood. The results are as follows: 1) Green tea leaves contained 9.85% of polyphenol compounds. 2) FT-IR results showed green tea leaves had effects to react with benzaldehyde and ethyl hexyl alcohol to form a chemical bond. 3) 2.5% of green tea leaves powder content was proper for scavenging effect on the UV varnishes and adhesives of fancy veneer overlaid on the PF resin bonded plywood 4) 20 liters small chamber test indicated excellent emission speed results such as
본 연구는 내구성이 우수하며 포름알데히드방출이 적은 페놀수지 사용 메란티합판을 마루판용 대판으로 사용하고 북미산 벚나무 단판을 표면재료로 사용한 마루판의 제조과정에서 접착제 및 도료에 녹차잎 분말을 첨가하였을 때 마루판으로부터 방출하는 총휘발성유기화합물(TVOC)과 포름알데히드의 감소효과와 녹차잎 분말의 적정 첨가량을 구명하였다. 1) 녹차잎 분말의 폴리페놀화합물량은 9.85%였다. 2) 녹차잎 분말은 FT-IR 결과 벤즈알데히드와 에틸헥사알콜과 반응하여 화학결합을 하는 것으로 나타났다. 3) 페놀수지메란티대판에 벚나무단판오버레이 마루판 제조를 위한 접착제와 UV도료에 전건중량기준으로 2.5%의 녹차잎 분말을 각각 첨가하는 것이 총휘발성유기화합물과 포름알데히드의 방산제거 효과가 매우 적절한 것으로 나타났다. 4) 20L 소형챔버법에 의한 녹차잎 분말 2.5%를 접착제와 도료에 각각 첨가한 온돌용 마루판의 7일째 TVOC는