Characterization Study of Various Solvents of Paraloid B72 for Bronze Artifacts Conservation by Surface Analysis

표면분석을 활용한 청동문화재 보존처리용 Paraloid B72의 용제별 특성 연구

We examined characterizations of Paraloid B72 films when it dissolved in four different solvents-acetone, MEK, toluene and xylene. The surface before and after coating were observed by optical microscope and AFM. Thickness and contact angle of films was measured and surface energy was calculated for grasping properties of films. We also tested adhesive strength of films by scratch tester and durability of films by performing yellowing test. The result was that xylene has better coating property than other solvents. Because 10% Paraloid B72 in xylene film is even, non-mottled, thin, stabilized in yellowish and has proper hydrophobic, we confirmed xylene is good solvent for bronze artifact conservation. However, other tests will need for finding appropriate concentration of Paraloid B72.

청동문화재 보존처리의 강화처리제로 가장 많이 쓰이고 있는 아크릴 수지인 Paraloid B72와 용제 4종(Acetone, MEK, Toluene, Xylene)을 선정하여 각 용제별 코팅 특성을 비교 분석하였다. 코팅 전 후의 표면을 현미경과 AFM을 통해 관찰하고 박막의 두께와 코팅 표면의 접촉각을 측정하여 표면에너지를 계산하였다. 그리고 Scratch Test를 통해 코팅 박막의 접착력을, 황변실험을 통해 코팅의 지속성을 조사하였다. 그 결과 Xylene을 용제로 사용하는 것이 육안으로 보았을 때 색 얼룩이 적고 적절한 소수성과 고른 표면을 가짐을 확인했다. 또한 코팅의 조건인 박막 두께가 얇으면서 접착력이 우수하며 황변에도 안정해야 한다는 점에서도 10% Paraloid B72 in xylene이 다른 용제에 비하여 우수한 코팅 성질을 가진다는 것을 확인하였다. 그러나 Paraloid B72의 적정농도를 찾기 위해서는 더 많은 실험과 분석이 이루어져야 할 것이다.