Study on production RDF using organic waste and peat-moss

유기성 폐기물과 피트모스를 이용한 고형연료 제조에 관한 연구

The purpose of this study is to derive the mixing ratio with stable heating value to be used as fuel and secondary fuel by mixing sewage sludge cake, tar, peat moss, and verify the combustion property of produced solid fuel and the applicability of RDF as alternative fuel. Tar shows the highest heating value with 7,000kcal/kg and the heating value of sewage sludge cake and peat moss ranges from 4,000 to 4,500kcal/kg. Also, the solid fuel with length 1.6cm, diameter 1.3cm and weight 2.3g was produced using the heating value of over 6,000kcal/kg and proper mixing ratio (sewage sludge cake: tar: peat moss) from 1 : 4 : 1 to 1 : 7 : 1. Upon the analysis of the RDF applicability of produced solid fuel, the exhaust gas analysis finds that the composition concentration of exhaust gas occurred according to the mixing ratio did not change significantly and the flame lasting time was found to be around 5 minutes, similar to the lasting time of the same mass (2.3g) of general anthracite burned. Therefore, it can be concluded that solid fuel produced in this study can be used as fuel and secondary fuel.

본 연구는 하수슬러지 케이크와 타르, 피트모스를 혼합하여 연료 및 보조연료로써 활용이 기능하도록 안정된 발열랑을 가지는 혼합비를 도출하고, 제조된 고형연료의 연소특성과 대체연료로써의 RDF의 적용가능성을 확인하는데 목적이 있다. 각각의 개별 발열량은 하수슬러지 케이크와 피트모스가 4000~4500kcal/kg 비슷하였으며, 타르의 발열량은 7000kcal/kg로 가장 높은 것으로 나타났다. 또한, 발열량 6,000kcal/kg 이상으로 하는 적정 혼합비를 (하수슬러지케이크 : 타르 : 피트모스) 1 : 4 : 1에서 1: 7 : 1까지로 하여 길이 1.6cm, 직경 1.3cm, 중량 2.3g의 고형연료를 제조하였다. 제조된 고형연료의 RDF 적용가능성 분석결과, 배기가스 분석에서는 혼합비에 따라 발생되는 배기가스의 성분농도가 크게 변하지 않았으며, 고형연료의 불꽃 지속시간은 5분 내외로 동일 질량 2.3g을 연소시킨 일반 무연탄과 지속시간이 비슷한 것으로 나타났다. 따라서 본 연구에서 제조한 고형연료의 연료 및 보조연료로서의 활용이 기능할 것으로 판단된다.