초록
Hydrogen storage properties of $Ti_{0.32}Cr_{0.43-X}V_{0.25}M_X$($0{\leq}X{\leq}0.1$, M=Fe, Mn, Si) have been investigated. With varing of Mn content, the lattice parameter of the alloy was unchanged and similar to that of $Ti_{0.32}Cr_{0.43}V_{0.25}$ alloy. With increase of Fe, Si content, the lattice parameters of the BCC phases decreased. When the Fe content was 8 at%, the desorption plateau pressure increased to several atmospheres without decrease of the effective hydrogen storage capacity of the alloy. When the Mn content was 8 at%, the effective hydrogen storage capacity showed approximately 2.5 wt% without change in the desorption plateau pressure. With increase of Si content, hysteresis increased and hydrogen storage capacity decreased rapidly. A study was also made on how desorption temperature affected the usable hydrogen of the $Ti_{0.32}Cr_{0.35}V_{0.25}Mn_{0.08}$ alloy. The temperature was varied from 293 to 413 K, and the pressure from 5 to 0.002 MPa. The usable hydrogen of the alloy was 2.7 wt% when absorbed and desorbed at 293 K and 373 K., respectively. The heat of hydride formation of the alloy was approximately -35.5 kJ/mol $H_2$.