Effect of Added Supercritical CO2 on the Characteristics of Copper Electroless Plating on PET Film Substrate

PET 필름기재의 구리 무전해도금에 있어서 초임계 CO2 유체가 도금 특성에 미치는 영향

  • Lee, Hee-Dai (Department of Chemical Engineering, Sungkyunkwan University) ;
  • Kim, Moon-Sun (Department of Chemical Engineering, Sungkyunkwan University) ;
  • Kim, Chul kyung (Department of Design & Materials, Mokwon University)
  • 이희대 (성균관대학교 화학공학과) ;
  • 김문선 (성균관대학교 화학공학과) ;
  • 김철경 (목원대학교 디자인소재학과)
  • 투고 : 2006.12.28
  • 심사 : 2007.05.07
  • 발행 : 2007.08.31
Download PDF
⟨ Previous Next ⟩

초록

In this study, electroless plating of copper was performed on PET film by using the blend of supercritical $CO_2$ and plating solution. The optimum volumetric ratio of supercritical fluid and plating solution was found to be 1:9 and dispersion property was poor at $CO_2$ vol% langer than 10%. Electroless plating of copper was best at $25^{\circ}C$ and 15 MPa. Role of added supercritical $CO_2$ is not to increase solubility but to disperse and maintain Cu-particles as the 1st particles.

본 연구는 $CO_2$ 초임계 유체를 도금액과 혼합하여 PET 필름 위에 무전해 구리도금을 실시하였으며 초임계 유체의 혼용조건에 따른 그 도금 효과를 비교하였다. 이산화탄소 초임계 유체와 도금액의 부피비는 1:9가 최적이였으며 초임계 유체가 10 vol% 이상이 되면 혼합액의 분산성이 불량해져 층분리가 발생하였다. 구리 무전해도금은 $25^{\circ}C$, 15 MPa 에서 수행된 구리막의 표면물성이 가장 균일하였다. 무전해 구리도금에서 도금액과 혼합시킨 초임계 유체의 역할은 단순히 용해도를 높여 주는 것이 아니라 도금막을 구성하는 구리입자를 1차 입자상태로 분산, 유지시킴을 확인하였다.

키워드

참고문헌

  1. Domenech, S. C., Jr. Lima, E., Drago, V., De Lima, J. C., Jr. Borges, N. G., Avila, A. O. V. and Soldi, V., 'Electroless Plating of Nikel-Phosphorous on Suface-Modified Poly(ethylene terephthalate) Films,' Appl. Surf. sci., 220, 238-250(2003) https://doi.org/10.1016/S0169-4332(03)00815-8
  2. Hong, K. M. and Chung, J. G., 'Study on Characteristics of Nikel Plating on Copper Substrate in Supercritical $CO_2$', J. Korean Ind. Eng. Chem., 15(3), 316-322(2004)
  3. Hong, K. M., Kim, M. S., Lee, Y. C. and Kim, N. K., 'The Characteristics of Nickel-Electroplating on Copper Substrate in $CO_2$ Supercritical Fluid,' J. MNM, 23, 247-250(2005)
  4. Lee, J. H., 'Wet Plating: Fundamentals and Applications of Electroplating and Electroless Plating,' Bul. Kor. Inst. Met. & Mater., 12(6), 658-666(1999)
  5. Lucien, F. P. and Foster, N. R., 'Solubility of Solid Mixtures in Supercritical Carbon Dioxide: A Revie,' J. Supercrit. Fluids, 17, 111-134(2000) https://doi.org/10.1016/S0896-8446(99)00048-0
  6. Ruckenstein, E. and Shulgin, I., 'Entrainer Effect in Supercritical Mixtures,' Fluid Phase Equilibria, 180, 345-359(2001) https://doi.org/10.1016/S0378-3812(01)00372-7
  7. Guerra, R. M., Marin, M. L., Sanchez, A. and Jimenez, A., 'Effect of Pressure, Temperature and Time on Supercritical Fluid Extraction of Citrate and Benzoate Plasticisers from Poly (vinyl chloride),' J. Supercrit. Fluids, 22, 111-118(2002) https://doi.org/10.1016/S0896-8446(01)00117-6
  8. Ruckenstein, E. and Shulgin, I., 'The Solubility of Solids in Mixtures Composed of a Supercritical Fluid and an Entrainer,' Fluid Phase Equilibria, 200, 53-67(2002) https://doi.org/10.1016/S0378-3812(02)00012-2
  9. Duarte, C. M. M., Crew, M., Casimiro, T. and Aguiar-Ricardo, A., 'Phase Equilibrium for Capsaicin +Water + Ethanol + Supercritical Carbon Dioxide,' J. Supercrit. Fluids, 22, 87-92(2002) https://doi.org/10.1016/S0896-8446(01)00114-0
  10. Akaishi, M., Shaji Kumar, M. D., Kanda, H. and Yamaoka, S., 'Formation Process of Diamond from Supercritical $H_2O-CO_2$ Fluid under High Pressure and High Temperature Conditions,' Diamond Relat. Mater., 9, 1945-1950(2000) https://doi.org/10.1016/S0925-9635(00)00366-6
  11. Caglar, A. and Demirbag, A., 'Conversion of Cotton Cocoon Shell to Liquid Products by Supercritical Fluid Extraction and Low Pressure Pyrolysis in the Presence of Alkalis,' Energy Conversion & Management, 42, 1095-1104(2001) https://doi.org/10.1016/S0196-8904(00)00122-9
  12. Guzel, B. and Akgerman, A., 'Mordant Dyeing of Wool by Supercritical Processing,' J. Supercrit. Fluids, 18, 247-252(2000) https://doi.org/10.1016/S0896-8446(00)00065-6
  13. Park, J. Y. and Lim, J. S., 'A Study on the Supercritical Carbon Dioxide Emulsion and Its Application,' Korean Chem. Eng. Res., 42(5), 494-509(2004)
  14. Yoshida, H., Sone, M., Mizushima, A., Yan, H., Wakabayashi, H., Abe, K., Tao, X. T., Ichihara, S. and Miyata, S., 'Application of Emulsion of Dense Carbon Dioxide in Electroplating Solution with Nonionic Surfactants for Nikel Electroplating,' Surf. Coat. Tech, 173, 285-292(2003) https://doi.org/10.1016/S0257-8972(03)00734-5
  15. Kim, M. S., Hong, K. M., Lee, Y. C., Kim, N. K. and Kim, C. K., 'Development of Nickel Plating Technology and Reduction Effect of Wastewater with Supercritical Nano-Plating System,' Korean J. EHS Assessment, 1(2), 35-51(2003)
  16. Park, J. Y., Kim, J. D., Lee, Y. W., Lee, C. H. and Lim, J. S., 'Studies on the Ni-Plating using Macroemulsion in Supercritical State,' Korean Chem., Eng. Res., 42(4), 396-403(2004)
  17. Kim, M. S. and Kim, C. K., 'Nickel Electroplating on Copper Substrating on Copper Substrate in Plating Solution Containing High-Density $CO_2$,' J. Ind. Eng. Chem., 11(6), 876-882(2005)
  18. Kim, M. S., Kim, J. Y. and Kim, C. K., 'Study on the Effect of Temperature and Pressure on Nickel-Electroplating Characteristics in Supercritical $CO_2$,' Chemosphere, 58, 459-465(2005) https://doi.org/10.1016/j.chemosphere.2004.09.030
  19. Oh, K. W., Kim, D. J. and Kim, S. H., 'Adhesion Improvement of Electroless Copper Plated Layer on PET Film -Effect of Pretreatment Conditions-,' Polymer, 25(2), 302-310(2001)
  20. Yan, H., Sone, M., Sato, N., Ichihara, S. and Miyata, S., 'The Effects of Dense Carbon Dioxide on Nickel Plating using Emulsion of Carbon Dioxide in Electroplating Solution,' Surf. Coat. Technol., 182, 329-334(2004) https://doi.org/10.1016/j.surfcoat.2003.07.006
  21. Park, J. Y., Kim, J. D., Lee, Y. W., Lee, C. H. and Lim, J. S., 'Studies on the Ni-Plating using Macroemulsion in Supercritical State,' Korean Chem. Eng. Res., 42(4), 396-403(2004)
  22. Schuh, C. A., Nieh, T. G. and Yamasaki, T., 'Hall-Petch Breakdown Manifested in Abrasive Wear Resistance of Nanocrystalline Nikel,' Scripta Materialia., 46, 735-740(2002) https://doi.org/10.1016/S1359-6462(02)00062-3
  23. Kim, M, S. and Lee, S. J., 'Characteristics of Porous Polycarbonate Membrane with Polyethylene Glycol in Supercritical $CO_2$ and Effect of Its Porosity on Tearing Stress,' J. Supercrit. Fluids, 31, 217-225(2004) https://doi.org/10.1016/j.supflu.2003.12.002
  24. Lou, X., Janssen, H. G. and Cramers, C. A., 'Temperature and Pressure Effects on Solubility in Supercritical Carbon Dioxide and Retention in Supercritical Fluid Chromatography,' J. Chromatogr., A785, 57-64(1997)
  25. Kim, J. R., Kim, H. K. and Kyong, J. B., 'Solubilities of Naphthalene in Supercritical Fluids,' J. Korean Chem. Soc., 32, 311-317(1988)
  26. Huang, Z., Guo, Y. H., Sun, G. B., Chiew, Y. C. and Kaw, S., 'Representing Dyestuff Solubility in Supercritical Carbon Dioxide with Several Density-Based Correlation,' Fluid Phase Equilibr., 236, 136-145(2005) https://doi.org/10.1016/j.fluid.2005.07.012
  27. Jiang, C., Pan, Q. and Pan, Z., 'Solubility Behavior of Solids and Liquids in Compressed Gases', J. Supercrit. Fluids, 12, 1-9(1998) https://doi.org/10.1016/S0896-8446(97)00042-9
  28. Lou, X., Janssen, H. G. and Cramers, C. A., 'Temperature and Pressure Effects on Solubility in Supercritical Carbon Dioxide and Retention in Supercritical Fluid Chromatography,' J. Chromatogr., 785, 57-64(1997) https://doi.org/10.1016/S0021-9673(97)00693-6