Removal Characteristic of Acidic Ion in Aqueous Solution by Alumina

알루미나에 의한 수용액 중의 산성이온 제거 특성

  • Received : 2007.05.30
  • Accepted : 2007.08.03
  • Published : 2007.10.10

Abstract

The removal characteristics of ionic species, such as $Ca^{2+}$, $Mg^{2+}$, $Sr^{2+}$, $SO{_4}^{2-}$, $NO{_3}^-$, and $Cl^-$ by adsorption on the alumina were investigated. Alumina precusor powders were prepared from $Al(NO_3)_3{\cdot}9H_2O$ and $NH_4OH$. Alumina materials prepared from the heat treatment in a furnace at $450{\sim}750^{\circ}C$ for 5 h were analysed using FT-IR and the Brunauer-Emmett-Teller (BET) method. The specific surface area of the product particles decreased significantly with treatment temperature. The adsorption capacities of $SO{_4}^{2-}$and $NO{_3}^-$ on alumina were 23 mg/g and 12.4 mg/g, respectively. But, removal efficiencies of $Cl^-$ were less than 4 mg/g. In general, the removal efficiencies of the anion species were decreased with increasing treatment temperature. The best anion removal efficiency was obtained when the alumina was treated under $450^{\circ}C$. Removal efficiencies of $Ca^{2+}$, $Mg^{2+}$, and $Sr^{2+}$ were increased with increasing treatment temperature.

본 연구는 알루미나를 이용하여 수용액 중에 존재하는 $Ca^{2+}$, $Mg^{2+}$, $Sr^{2+}$, $SO{_4}^{2-}$, $NO{_3}^-$, $Cl^-$ 이온의 제거 특성을 분석하기 위하여 실시하였다. 알루미나는 $Al(NO_3)_3{\cdot}9H_2O$$NH_4OH$를 사용하여 합성한 수화물을 $450{\sim}750^{\circ}C$로 5 h 동안 열처리하고 FT-IR과 Brunauer-Emmett-Teller (BET)법으로 물성을 분석하였다. 실험결과에 의하면 알루미나의 비표면적은 열처리 온도가 증가하면 감소하는 특성을 나타내었다. 알루미나에 의한 흡착능은 $SO{_4}^{2-}$$NO{_3}^-$가 각각 23 mg/g와 12.4 mg/g의 값을 보였다. 반면에 $Cl^-$는 4 mg/g으로 비교적 낮은 값을 보였다. 일반적으로 음이온 제거 효율은 알루미나의 제조를 위한 열처리 온도가 증가할수록 감소하였으며, $450^{\circ}C$로 처리한 알루미나의 경우에 가장 좋은 처리 효율을 나타내었다. 양이온인 $Ca^{2+}$, $Mg^{2+}$, $Sr^{2+}$의 제거 효율은 알루미나의 열처리 온도에 비례하여 증가하는 경향을 보였다.

Keywords

Acknowledgement

Supported by : 혜전대학

References

  1. B. Ksapabutr, E. Gulari, and S. Womgkasemjit, Colloid and Surface, 53, 145 (2004)
  2. J. Temuujin, Ts. Jadambaa, K. J. D. Mackenzie, P. Angerer, and F. Porte, Bull. Mater. Sci., 23, 301 (2000) https://doi.org/10.1007/BF02720086
  3. L. D. Hart, Alumina Chemicals: Science and Technology Handbook, The American Ceramic Society, Ohio (1990)
  4. A. L. Carre, F. Roger, and C. Varinot, J. Colloid & Interface Sci., 154, 174 (1992)
  5. J. A. Mieth, J. A. Schwarz, Y. T. Huang, and S. C. Fung, J. Catal., 122, 202 (1990) https://doi.org/10.1016/0021-9517(90)90272-L
  6. R. Sprycha, J. Colloid & Interface Sci., 123, 1 (1989)
  7. B. S. Umansky and W. K. Hall, J. of Catalysis, 124, 97 (1990) https://doi.org/10.1016/0021-9517(90)90106-T
  8. S. Subramanian, J. S. Noh, and J. A. Schwarz, J. Catal., 114, 433 (1988) https://doi.org/10.1016/0021-9517(88)90046-2
  9. J. A. Nattanson, Basic Environmental Technology, 92, Prentice Hill, New Jersey (2000)
  10. S. Y. Kim, J. H. Kim, H. J. Kim, and Y. S. Cho, J. of K. S. E. E., 27, 247 (2005)
  11. J. H. Moon, C. H. Choi, B. R. Ryu, and C. G. Kim, J. of K. S. E. E., 27, 1058 (2005)
  12. M. R. Sudhakar and P. Mamatha, Current Science, 87, 942 (2004)
  13. S. A. Kim, J. S. Hong, J. K. Suh, H. Kang, and J. M. Lee, J. of K. S. E. E., 27, 109 (2005)
  14. H. J. Son, J. S. Roh, S. G. Kim, S. M. Bae, and L. S. Kang, J. of K. S. E. E., 27, 762 (2005)
  15. M. Yurdakoc, M. Akcay, Y. Tonbul, and K. Yurdakoc, Turk J. Chem., 23, 319 (1999)