Abstract
A wallpaper having many surfaces in indoor is composed of various raw materials. In this study, TVOC contribution from raw materials of PVC wallpaper was evaluated by using headspace-solid phase microextraction (HS-SPME)-GC/MS. Samples were diluent, resin stabilizer, plasticizer, filler, blowing agent and PVC resin. 9 mL of each sample was put into 22 mL glass vial and they were equilibrated for 1 hour at $100^{\circ}C$. Headspace in vial was absorbed to $75{\mu}m$ Carboxen-PDMS fiber and analyzed by GC/MS. Aromatic compounds like a toluene, ethylbenzene and xylene, ketones compounds like a acetone, methoxyacetone and 2-butanone and alkane compounds like a nonane decane and undecane were identified from raw materials. And alcohol compounds like a ethanol and butanol and aldehydes were detected. TVOC emission of diluent, resin stabilizer, plasticizer, PVC resin, blowing agent and filler were $54.20{\mu}g/g$, $32.88{\mu}g/g$, $0.50{\mu}g/g$, $0.88{\mu}g/g$, $0.22{\mu}g/g$ and $0.11{\mu}g/g$, respectively. Contribution of TVOC emission of diluent, resin stabilizer and PVC resin that were concerned about add ratio were 0.708, 0.129, 0.115, respectively. In conclusion, it's necessary to reduce TVOC emission through improvement of diluent, resin stabilizer and PVC resin. Also, HS-SPME-GC/MS method which was developed in this study will be used for raw materials analysis effectively.
본 연구에서는 headspace-solid phase microextraction(HS-SPME)-GC/MS법을 이용하여 PVC 벽지의 원자재에서 방출되는 TVOC를 분석하여 기여도를 평가하였다. 시료로 사용한 원자재는 6종으로 희석제, 안정제, 가소제, 충전제, 발포제와 PVC 레진이다. 각 원자재 시료를 22 mL 바이알에 9 mL씩 취한뒤 $100^{\circ}C$에서 1시간동안 평형을 이룬 다음 $75{\mu}m$ Carboxen-PDMS 화이버로 $25^{\circ}C$에서 1시간 흡착하여 GC/MS로 분석하였다. 정성결과 toluene, ethylbenzene 그리고 xylene과 같은 방향족 화합물과 acetone, methoxyacetone, 2-butanone 등의 케톤류와 nonane, decane, undecane 등의 알켄류가 검출되었다. 그 밖에도 ethanol, butanol 등의 알콜류와 알데히드류 등이 검출되었다. TVOC 방출량은 희석제 $54.20{\mu}g/g$, 안정제 $32.88{\mu}g/g$, 가소제 $0.50{\mu}g/g$, PVC 레진 $0.88{\mu}g/g$, 발포제 $0.22{\mu}g/g$, 충전제가 $0.11{\mu}g/g$로 나타났다. 각 원자재의 TVOC 방출량과 배합비를 고려한 TVOC 기여도는 희석제 0.708, 안정제 0.129, PVC 레진 0.115 순으로 높게 나타났다. 따라서 희석제와 안정제, PVC레진의 질적인 개선을 통해 TVOC 방출량을 줄이는 노력이 필요하다. 또한 본 연구에서 개발한 HS-SPME-GC/MS 방법은 원자재의 TVOC 분석에 유용하게 사용될 것으로 생각된다.