Experimental Study of Freezing Characteristics and Antifreezing Method of Liquid Additive for Early Strength

액상형 조강제의 동결특성 및 동결방지 방안에 관한 실험적 고찰

In ready mixed concrete factory, in case of using the high molecular additive in winter especially the liquid additive for the early strength, it is required to check the stability. In this research, the freezing and gelling characteristics of the liquid additive for the early strength is reviewed, the material and mechanical solution are proposed to that the practical quality control method will be suggested. As the result, the Freezing temperature of the liquid additive for the early strength is $-11.8^{\circ}C$, and it is the lower than the temperature at which the strength is shown. By making with sodium silicate of $37{\pm}0.5%$ designed by $SiO_2\;and\;Na_2O$ in 0.31 of mol ratio, it minimizes the gelling at the lower temperature. On the other hand, facilities for storing and supplying the material should be set at $40^{\circ}C$ so the temperature distribution is well spreaded for practical operation.

레디믹스트콘크리트 공장에서 동절기에 고분자 화학 혼화제, 특히 조기강도 확보를 위해 개발된 액상형 조강제를 사용할 경우, 해당 혼화제의 저장 안정성을 검토할 필요가 있다. 본 연구에서는 액상형 조강제의 동결 및 겔화 특성을 검토하고, 이를 방지할 수 있는 재료적, 설비적 해결 방안을 제시하여, 실무 적용시의 품질관리 방안으로 제시하고자 하였다. 검토 결과, 액상형 조강제의 동결온도는 $-11.8^{\circ}C$ 정도로 확인되어 콘크리트의 강도 발현 온도한계보다 낮은 온도 범위로서 안정적인 것을 확인하였으며, $SiO_2$와 $Na_2O$의 mol비를 0.31 수준으로 디자인한 sodium silicate를 $37{\pm}0.5%$ 포함시켜 제조함에 따라 저온에서의 겔화를 최소화하는 한편, 이의 저장 및 공급을 위해 고안된 설비 시설은 공급탱크의 온도를 $40^{\circ}C$ 정도로 설정하여 설비 전단계의 온도 분포가 실무 활용상 문제가 없음을 확인할 수 있었다.