Abstract
The purpose of this study is to clarify the effect of the monomer ratio on properties of the polymer-modified mortars based on styrene and butyl acrylate latexes, and to obtain basic data necessary to develop appropriate latexes for cement modifiers. This paper deals with the effects of monomer ratio on the typical properties of the polymer-modified mortars with styrene and butyl acrylate latexes. The polymer-modified mortars using the styrene and butyl acrylate latexes polymerized with various monomer ratios are prepared with different polymer-cement ratios, and tested for the particle size of polymer latexes, air contents, water-cement ratios, flexural and compressive strengths, water absorption, and chloride-ion penetration. From the test results, the polymer-modified mortars using styrene and butyl acrylate latexes with the mix proportions of synthesis having monomer ratios of 50:50 to 60:40 for the appropriate mix proportions can be recommended for practical applications. Their basic properties are greatly affected by the polymer-cement ratio rather than the monomer ratio, and are improved over un-modified mortar.
본 연구에서는 스틸렌(styrene)과 부틸아크릴레이트(butyl acrylate)를 모노머 비에 따라 합성 제조하고, 합성 제조 된 시멘트 혼화용 폴리머를 혼입한 폴리머 시멘트 모르타르의 물리적 성질과 내구성에 대한 특성을 보통 시멘트 모르타르와 기존에 생산되어 현장에 적용되고 있는 St/BA계 폴리머 시멘트 모르타르를 비교 분석하고자 하였다. 실험 결과, St/BA의 모노머 비가 50:50, 60:40일 경우에는 시멘트 혼화용으로 사용하기에 가장 적합하였으며, 세공용적의 분포나 강도 특성에서도 우수한 결과를 나타냈다. 또한 방수성능과 염화물 이온에 대한 침투 저항성도 St/BA의 모노머비가 증가할수록, 폴리머 시멘트 비가 증가할수록 증진 효과가 우수한 결과를 나타냈다. 따라서 본 연구를 통해 합성제조된 St/BA 라텍스를 시멘트 모르타르에 혼입할 경우 우수한 성능개선 효과를 얻을 수 있었다.