Removal of SO2 over Binary Nb/Fe Mixed Oxide Catalysts

이성분계 Nb/Fe 혼합산화물 촉매에 의한 아황산가스의 제거

  • Chung, Jong Kook (Faculty of Applied Chemical Engineering, Pukyong University) ;
  • Lee, Seok Hee (Faculty of Applied Chemical Engineering, Pukyong University) ;
  • Park, Dae Won (Department of Chemical Engineering, Pusan University) ;
  • Woo, Hee Chul (Faculty of Applied Chemical Engineering, Pukyong University)
  • 정종국 (부경대학교 응용화학공학부) ;
  • 이석희 (부경대학교 응용화학공학부) ;
  • 박대원 (부산대학교 화학공학과) ;
  • 우희철 (부경대학교 응용화학공학부)
  • Received : 2006.05.18
  • Accepted : 2006.06.19
  • Published : 2006.06.30
Download PDF
⟨ Previous Next ⟩

Abstract

The reduction of $SO_2$ to elemental sulfur by CO over a series of iron niobate with nominal Nb/Fe atomic ratios of 1/0, 10/1, 5/1, 1/1, 1/5, 1/10 and 0/1 was studied with a flow fixed-bed reactor. Strong synergistic phenomena in catalytic activity and selectivity were observed for the iron niobate catalysts, and the best catalytic performance was observed for the catalyst with Fe/Nb atomic ratio of 1/1. The active phase of the activated iron niobate catalysts was identified to be $FeS_2$ using XRD and XPS. Selective reduction of $SO_2$ by CO was followed by the COS intermediate mechanism.

철과 니오븀의 몰비가 1/0, 10/1, 5/1, 1/1, 1/5, 1/10 및 0/1 인 철-니오븀 촉매상에서 일산화탄소에 의한 아황산가스의 원소 황으로의 환원이 고정층 흐름반응기에서 연구되었다. 촉매 활성 및 선택도 면에서 우수한 상승효과를 철-니오븀 촉매에서 관찰할 수 있었으며, 가장 우수한 촉매 현상은 철과 니오븀의 몰비 1/1 촉매에서 관찰되었다. 활성화된 철-니오븀 촉매의 활성상은 XRD와 XPS 의 분석결과 $FeS_2$ 로 확인되었다. 일산화탄소에 의한 아황산가스의 선택적 환원은 카르보닐 황화물 반응중간체 메커니즘을 따르는 것으로 나타났다.