Ring-Opening Polymerization of ʟ-Lactide with Polydimethylsiloxane Based Stabilizers in Supercritical Carbon Dioxide

폴리디메틸실록산계 안정화제를 이용한 초임계 이산화탄소에서의 ʟ-Lactide의 개환중합

  • Hwang, Ha Soo (Division of Image and Information Engineering, Pukyong National University) ;
  • Lim, Kwon Taek (Division of Image and Information Engineering, Pukyong National University)
  • 황하수 (부경대학교 화상정보공학부) ;
  • 임권택 (부경대학교 화상정보공학부)
  • Received : 2006.02.03
  • Accepted : 2006.06.05
  • Published : 2006.06.30
Download PDF
⟨ Previous Next ⟩

Abstract

Poly($\small{L}$-Lactide)(PLLA) was prepared by a ring-opening polymerization of $\small{L}$-Lactide with various polydimethylsiloxane(PDMS) based copolymers as a stabilizer in supercritical carbon dioxide($scCO_2$). The block copolymeric stabilizers were synthesized by group transfer polymerization (GTP) by using PDMS macroinitiator. PLLA was found to be produced with fairly low molecular weight distribution as confirmed by gel permeation chromatography(GPC) analysis. Scanning electron microscopy (SEM) results showed that sub-micron size Poly($\small{L}$-lactide)(PLLA) particles were formed by suspension polymerization.

다양한 폴리디메틸실록산계 공중합체를 안정화제로 이용하여 초임계 이산화탄소 내에서의 개환중합을 통해 PLLA를 제조하였다. 초임계 개환중합에 사용된 폴리디메틸실록산 공중합체는 폴리디메틸실록산 거대개시제를 사용하여 그룹전이중합법(GTP법)을 이용하여 제조하였다. $\small{L}$-락타이드의 초임계 현탁중합을 통해 수미크론크기의 입자가 형성되었음을 전자 주사 현미경을 통해 확인하였고, 또한 겔 투과 크로마토 그라피 분석을 통해 상당히 좁은 분자량 분포의 PLLA가 제조되었음을 확인하였다.