Water vapour permeable and water resistant film was laminated to made footwear woven fabric and non-woven fabrics by screen type with thermosetting reactive hot melt adhesive. Optimum conditions of each process were investigated, and the properties of film laminated fabric with optimum conditions are evaluated. The results are as follows. Thermosetting reactive polyurethane hot melt is retain proper heat resistance differently thermoplastic hot melt. Optimum melting adhesive process conditions are as follows ; drum temperature $95^{\circ}C$, hose temperature $97^{\circ}C$, feeding pipe temperature $100^{\circ}C$, screen temperature $105^{\circ}C$, pressure of opposite roller $1kgf/cm^2$, pressure of laminating roller $3kgf/cm^2$, finishing speed 15 m/min, melting temperature $120^{\circ}C$, cooling time 20 s, pressing temperature $130^{\circ}C$, pressing time 30 s. As the thickness of film was increased, the water vapour permeability was decreased but water resistance was increased, and the effect of film is dominant over all the others in the air permeability.

내열성 및 투습방수기능을 가진 신발용 직물 및 부직포를 제조하기 위하여 스크린 방식으로 공정조건을 검토하고 투습방수 필름을 라미네이팅 한 후, 최종제품의 물성을 평가하였다. 결과는 다음과 같다. 열가소성 핫 멜트와는 달리 반응형 폴리우레탄 핫 멜트는 작업 이후에 적정한 내열성을 보유하는 것으로 나타났다. 최적의 용융접착 공정조건은 다음과 같다 ; 드럼 온도 $95^{\circ}C$, 호스 온도 $97^{\circ}C$, 공급파이프 온도 $100^{\circ}C$, 스크린 온도 $105^{\circ}C$이고, opposite roller의 압력은 $1kgf/cm^2$, laminating roller의 압력은 $3kgf/cm^2$이며, 가공속도는 15 m/min이다. 투습도는 필름의 두께가 증가함에 따라 투습도는 감소하였으나, 내수도는 증가하였고, 공기투과도는 필름의 영향이 지배적이었다.