Preparation and Properties of Water-borne PU Having Ionic Center onto Flexible Side Chain

유연한 곁가지 말단에 이온성 작용기를 가지는 양이온성 수분산 PU의 제조와 물성

  • Kim, Dong-Min (Department of Advanced Material Engineering, College of Engineering, Kongju National University) ;
  • Bang, Moon-Soo (Department of Advanced Material Engineering, College of Engineering, Kongju National University) ;
  • Kim, Hyung-Joong (Department of Advanced Material Engineering, College of Engineering, Kongju National University)
  • 김동민 (공주대학교 공과대학 신소재공학부) ;
  • 방문수 (공주대학교 공과대학 신소재공학부) ;
  • 김형중 (공주대학교 공과대학 신소재공학부)
  • Received : 2006.01.06
  • Accepted : 2006.01.25
  • Published : 2006.03.30
Download PDF
⟨ Previous Next ⟩

Abstract

Three isocyanate groups of IP-$75^{(R)}$ and one hydroxyl group of various amino alcohols were applied for preparing cationic type water-borne polyurthane (PU) having ionic center onto flexible side chains. Average particle size, dispersion stability, viscosity, contact angle, surface energy, glass transition temperature ($T_g$), and adhesion strength of prepared water-borne PUs were measured and analyzed with different NCO/OH mol ratios, ionomers, and neutralizing agents. It was characterized that the prepared PU has a smaller particle size and a better dispersion stability than the conventional cationic water-borne PU containing ionic centers onto main chains.

세 개의 isocyanate작용기를 가지는 IP-$75^{(R)}$와 하나의 hydroxyl작용기를 가지는 여러 가지 amino alcohol을 ionomer로 이용하여 수분산에 필요한 ionic center가 측쇄에 위치하는 양이온성 수분산 polyurethane (PU)을 합성하였다. NCO/OH몰 비, ionomer의 종류 및 중화제의 종류에 따라 수분산 PU의 입도, 점도, 분산안정성, 접촉각, 표면에너지, $T_g$, 그리고 접착강도의 변화를 알아보았다. 제조된 수분산 PU는 주쇄에 ionic center를 가지는 양이온 수분산 PU보다 더 작은 입도를 가지며 분산안정성도 우수함을 확인하였다.