Abstract
In this study, in order to develop the multilayer piezoelectric actuator and ultrasonic resonator, PMN-PNN-PZT ceramics were fabricated by sintering with $Li_2CO_3-Na_2CO_3$ as sintering aids at $950^{\circ}C$ and their piezoelectric and dielectric characteristics were investigated as a function of PNN substitution. With increasing PNN substitution, dielectric constant(${\epsilon}_r$), electromechanical coupling factor(kp), and piezoelectric d constant($d_{33}$) were increased to $12 mol\%$ PNN substitution and then showed a tendency to decrease rapidly With increasing PNN substitution, crystal structure changed from tetragonal to rhombohedral at $12 mol\%$ PNN substitution and then secondary phase was appeared and its intensity was increased. At the $12 mol\%$ PNN substituted PMN-PZT composition ceramic sintered at $950^{\circ}C$, density, kp, $d_{33}$ and Qm showed the optimum value of $7.79 g/cm^3$, 0.599, 419 pC/N, and 894, respectively for multilayer piezoelectric actuator application.