SM490B 용접부의 피로균열 성장 거동에 미치는 초고속 용사코팅 효과

The Effect of High Velocity Oxygen Fuel Thermal Spray Coating on Fatigue Crack Growth Behavior for Welded SM490B

  • 윤명진 (경일대학교 기계자동차학부) ;
  • 최성종 (경일대학교 기계자동차학부) ;
  • 조원익 (경일대학교 기계자동차학부)
  • Yoon, Myung-Jin (School of Mechanical & Automotiv Engineering, Kyungil University) ;
  • Choi, Sung-Jong (School of Mechanical & Automotiv Engineering, Kyungil University) ;
  • Cho, Won-Ik (School of Mechanical & Automotiv Engineering, Kyungil University)
  • 발행 : 2006.07.01

초록

High velocity oxygen-fuel thermal spray coating of the WC-Co cermet material is a well-established process for modifying the surface properties of the structural components exposed to the corrosive and wear attacks, and also these coating are well-known method to improve the fatigue strength of material. In this study, HVOF coated SM490B are prepared to evaluation of the effect of coating on tension and fatigue crack growth behavior. The pre-crack of the fatigue crack growth test specimens machined at deposited material area, heat affected zone and boundary, respectively. Through these test, the following results are obtained: 1) Tensile strength was about 498 MPa, and fracture occurred on base metal area. 2) The fatigue crack of coated specimens propagated more rapidly than non-coated specimen in all specimens. 3) In the same coating thickness specimens, the specimens with pre-crack at boundary more rapidly propagated than the specimens with pre-crack at HAZ and deposited material area. These results can be used as basic data in a structural integrity evaluation of rolled SM490B weldments considering HVOF coating.

키워드

참고문헌

  1. Sindo Kou, Welding Metallurgy, p.170, John Wiley & Sons, Inc., New York, 2002
  2. Japan Welding Society, Fractographic Atlas Steel Weldments, Kuroki, Osaka, p.70, 1982
  3. R. I. Stephens, A. Fatemi, R. R. Stephens and H. O. Fuchs, Metal Fatigue in Engineering, John Wiley & Sons, New York, p.401, 2000
  4. L. A. James and W. J. Mills, 'Effect of Heat - Treatment upon the Fatigue Crack Growth Behavior of Alloy 718 Weldments, Part 1: Macroscopic Behavior,' J. of Eng. Mat. and Tech., Trans. of ASME, Vol.107, p.34, 1985 https://doi.org/10.1115/1.3225768
  5. W. J. Mills and L. A. James, 'Effect of Heat - Treatment upon the Fatigue Crack Growth Behavior of Alloy 718 Weldments, Part 2: Microscopic Behavior,' J. of Eng. Mat. and Tech., Trans. of ASME, Vol.107, p.41, 1985 https://doi.org/10.1115/1.3225769
  6. C. H. Kim, S. Y. Cho and D. H. Bae, 'Evaluation of Fatigue Crack Charistics Considering Crack Closure Phenomenon in Weldment of Multi-Pass Welded Pipe,' Trans. of the Korean Soc. of Mech. Engineers A, Vol.25, No.5, p.797, 2001
  7. S. H. Han, J. W. Han, B. C. Shin and J. H. Kim, 'Fatigue Life Estimation of Welded Components Considering Welding Residual Stress Relaxation and its Mean Stress Effect,' Trans. of the Korean Soc. of Mech. Engineers A, Vol.27, No.1, p.175, 2003 https://doi.org/10.3795/KSME-A.2003.27.1.175
  8. M. S. Han, 'A Study on Fatigue Fracture Behavior of Surface Crack in Finite Plates and Fillet Weldment,' Trans. of the Korean Soc. of Automotive Engineers, Vol.12, No.4, p.65, 2004
  9. M. Araki, COATING, CTI-Kakoukenkyukai, Tokyo, 2002
  10. L. Pawlowski, The Science and Engineering of Thermal Spray Coating, John Wiley & Sons, New York, 1995
  11. S. Y. Hwang, B. G. Seong and M. C. Kim, 'R&D Trends of Thermal Sprayed Coatings,' J. of Korean Powder Metallurgy Institute, Vol.3, No.2, p.79, 1996
  12. J. S. Oh, J. Komotori and C. K. Rhee, 'Effect of Post-heat Treatment on Fatigue Strength of Thermally Sprayed Stellite Alloy on Steel,' J. of Korean Powder Metallurgy Institute, Vol.12, No.2, p.106, 2005 https://doi.org/10.4150/KPMI.2005.12.2.106
  13. Y. D. Jeong, W. I. Cho, M. J. Yoon and B. M. Kim, 'The Processing Parameters of HVOF and Optimal Characteristics Coating Condition,' The J. of KASBIR, Vol.4, No.4, p.47, 2003
  14. R. Koterazawa, Fractography and Application, p.266, Nikankogyosinbunsya, Tokyo, 1981