Fabrication and Characterization of Yellow OLED using GDI602:Rubrene(10%) Material

GDI 602/Rubrene을 이용한 황색 OLED의 제작과 특성 분석

The yellow emitting OLED using GDI602:Rubrene(10%) material has been fabricated and characterized. In the device fabrication, 2-TNATA [4,4',4'-tris(2-naphthylphenyl-phenylamino)-triphenyl-amine] as a hole injection material and NPB[N,N'-bis(1-naphthyl)-N,N'-diphenyl-1,1'-biphenyl -4,4'-diamine] as a hole transport material were deposited on the ITO(indium thin oxide)/glass substrate by vacuum evaporation. And then, yellow emission material was deposited using GDI602 as a host material and Rubrene(10%) as a dopant. Finally, small molecular OLED with the structure of $ITO/2-TNATA/NPB/GDI602:Rubrene(10%)/Alq_{3}/LiF/Al$ was obtained by in-situ successive deposition of $Alq_{3}$, LiF and Al as the electron transport material, electron injection material and cathode. The yellow OLED fabricated in our experiments showed the color coordinate of CIE(0.50, 0.49), the luminance of $2300\;Cd/m^{2}$ and the power efficiency of 0.7 lm/W at 10 V with the peak emission wavelength of 562 nm.

GDI602:Rubrene(10%) 형광 시스템을 이용하여 황색 발광 OLED를 제작하고 그 특성을 평가하였다. 소자 제작에서 ITO/glass 위에 정공 주입층으로 2-TNATA[4,4',4'-tris(2-naphthylphenyl-phenyl-amino)-triphenylamine]를, 정공 수송층으로 NPB[N,N'-bis(1-naphthyl)-N,N'-diphenyl-1,1'-biphenyl-4,4-diamine]를 진공 증착하였다. 황색 발광층으로는 GDI602를 호스트로, Rubrene를 도펀트로 사용하였다. 또한, 전자 수송층으로는 $Alq_{3}$를, 전자 주입층으로는 LiF를 사용하여 $ITO/2-TNATA/NPB/GDI602:Rubrene(10%)/Alq_{3}/LiF/Al$ 구조의 저분자 OLED를 제작하였다. 본 실험에서 제작된 황색 OLED는 562nm의 중심 발광 파장을 가지며, CIE(0.50, 0.49) 색순도, 그리고 10V의 동작전압에서 $2300\;Cd/m^{2}$ 휘도와 0.7 lm/W의 전력 효율을 나타내었다.