Pressure Sensitive Adhesion Performances of SIS/SBS based UV-curable Pressure Sensitive Adhesives using Thiol-ene Reaction

Thiol-ene 반응을 이용한 UV경화형 SIS/SBS계 점착제의 점착물성

  • Lim, Dong-Hyuk (Lab. of Adhesion & Bio-Composites, Major in Environmental Materials Science, Seoul National University) ;
  • Do, Hyun-Sung (Lab. of Adhesion & Bio-Composites, Major in Environmental Materials Science, Seoul National University) ;
  • Kim, Hyun-Joong (Lab. of Adhesion & Bio-Composites, Major in Environmental Materials Science, Seoul National University) ;
  • Yoon, Goan-Hee ;
  • Bang, Jung-Suk
  • 임동혁 (서울대학교 환경재료과학 전공 바이오복합재료 및 접착과학 연구실) ;
  • 도현성 (서울대학교 환경재료과학 전공 바이오복합재료 및 접착과학 연구실) ;
  • 김현중 (서울대학교 환경재료과학 전공 바이오복합재료 및 접착과학 연구실) ;
  • 윤관희 ((주)빅솔) ;
  • 방정석 ((주)빅솔)
  • Received : 2005.08.02
  • Accepted : 2005.09.15
  • Published : 2005.09.25
Download PDF
⟨ Previous Next ⟩

Abstract

Synthetic rubber based pressure-sensitive adhesives (PSAs) usually containing SIS or SBS block copolymer, tackifier, plasticizer, and other additives are now widely used on various applications. As these PSAs are physically crosslinked and can be applied without the use of solvent, they are thermally processable and environmentally friendly. However these PSAs cannot be used in high temperature applications and in applications where solvent and chemical resistance properties are required. We developed the PSA adding UV curable system, such as thiol-ene system, to increase adhesion properties at elevated temperature. The adhesion properties such as probe tack, peel strength, shear adhesion failure temperature (SAFT) were evaluated. The probe tack test was conducted with varying probe materials and coating thickness of PSAs. Using the contact angle, the surface property of the cured PSAs was also observed.

합성 고무계 점착제는 일반적으로 SIS나 SBS 블록 공중합체와 점착부여수지, 가소제, 기타 첨가제를 함유한다. SIS/SBS 계 점착제는 우수한 접착력에도 불구하고 내용제성이나 내열성이 낮아서 그 사용에 한계가 있다. 이에 이러한 단점을 보완하고자 SIS/SBS 점착제에 가교제, 광개시제를 주성분으로 하는 자외선 경화 시스템을 도입하였다. 제조된 점착제는 thiol-ene 광중합 반응에 의해 가교하였으며 점착제의 프로브 택(probe tack), 박리강도(peel strength) 전단접착파괴온도(shear adhsion failure temperature, SAFT)를 측정하여 UV 경화형 점착특성을 고찰하였다. 또한 UV 경화형 점착제의 택 성질을 프로브 택을 이용하여 프로브 재료별, 점착제의 두께별의 영향을 살펴보았고 접촉각 측정을 통해 점착제 표면 변화를 살펴보았다.