Effect of Silicon on the Processing Window of High Carbon High Silicon Steels

  • Kim, Won-Bae (Department of Materials Science and Metallurgy, Kyungpook National University) ;
  • Ming, Xing (Department of Materials Science and Metallurgy, Kyungpook National University) ;
  • Moon, Yong-Min (BNG Steel Co. Ltd.) ;
  • Kim, Jong-Chul (R&D Center, Hwashin Co. Ltd.) ;
  • Sohn, Ho-Sang (Department of Materials Science and Metallurgy, Kyungpook National University) ;
  • Ye, Byung-Joon (Department of Materials Science and Metallurgy, Kyungpook National University)
  • 발행 : 2005.06.20
PDF 다운로드
⟨ 이전 논문 다음 논문 ⟩

초록

0.8wt.% C과 $0.75{\sim}3.2$(0.75, 1, 1.26, 1.44, 1.89, 2.1, 2.46, 2.94, 3.22)wt.% Si을 함유한 고탄소 고실리콘 강에서 Si의 함량이 미세조직과 processing window에 미치는 영향에 대해 조사하였다. 열처리는 $940^{\circ}C$에서 1시간 동안 오스테나이징을 실시한 후, $320^{\circ}C$에서 $0.2{\sim}300$분 동안 오스템퍼링을 하였다. 미세조직에서, 0.75 wt.% Si을 함유한 강에서 국부적으로 오스페라이트(ausferrite)가 존재하는 것을 확인하였다. Processing window는 경도 및 XRD 측정으로 결정하였다. $t_{1}$은 Si의 함량이 2.5 wt.% 이하에서는 거의 변화가 없다가,2.5 wt.% 이상에서는 감소하는 결과를 보였다. 반면, $t_{2}$는 Si의 함량이 증가함에 따라 연속적으로 증가하였다. 즉, 0.8 wt.% C을 함유한 강에서 processing window는 Si의 함량이 약 2.5 wt.%일 때 열렸다.

키워드

참고문헌

  1. R. C. Voigt and C. R. Loper, Jr.: Proceedings, 1st international Conference Austempered Ductile Iron, ASM, Metal Park, OH (1984), 83
  2. A. S. Hamid Ali, R. Elliott : Mat. Sci. Tech., 'Austempering of an Mn-Mo-Cu alloyed ductile iron Part 2-structure-mechanical property relationships', 12 (1996) 780-787 https://doi.org/10.1179/026708396790122404
  3. J. M. Velez, A. Garboggini and A. D. Tschiptschin : Mater. Sci. Tech., 'Effect of Silicon on Kinetics of Bainitic Reaction in Austempered Ductile Cast Iron', 12 (1996) 329-337 https://doi.org/10.1179/mst.1996.12.4.329
  4. R. C. Vogit, R. Bendaly, J. F. Janowak, Y. J Park : AFS Trans., 'Development of Austempered High Silicon Cast Steels', 93 (1987) 85-72
  5. Yanxiang Li and Xiang Chen : Mat. Sci. Eng., A, 'Micorstructure and mechanical properties of austempered high silicon', 308 (2001) 277-282 https://doi.org/10.1016/S0921-5093(00)01779-2
  6. Susil K. Putatunda : Mat. Sci. Eng., A, 'Fracture toughness of a high carbon and high silicon steel', 297 (2001) 31-43 https://doi.org/10.1016/S0921-5093(00)01272-7
  7. S. Yazdani and R. Elliott : Mater. Sci. Tech., 'Influence of Molybdenum on Austempering Behaviour of Ductile Iron Part 1-Austempering Kinetics and Mechanical Properties of Ductile Iron Containing 0.13%Mo', 15 (1999) 531-541 https://doi.org/10.1179/026708399101506247
  8. R.C. Voigt and C.R. Loper, Jr.: J. Heat Treat., 3(4) (1984), 291 https://doi.org/10.1007/BF02833124
  9. D.J. Moor, T.N. Rouns and K.B. Roundman : AFS Trans., 'Effect of Manganese on Structure and Properties of Austempered Ductile Iron : A Processing Window Concept', 125 (1986) 255-264