Modulus Properties and Smoothness Measurement of Semiconducting Materials Using the DMA and SEM

DMA와 SEM을 사용한 반도전층 재료의 탄성특성과 평활도 측정

  • 양종석 (원광대 전기전자및정보공학부) ;
  • 이경용 (원광대 전기전자및정보공학부) ;
  • 최용성 (원광대 전기전자및정보공학부) ;
  • 박대희 (원광대 전기전자 및 정보공학부)
  • Published : 2005.10.01
Download PDF
⟨ Previous Next ⟩

Abstract

To measure modulus, damping properties and smoothness of semiconducting materials in power cable, we have investigated those of semiconducting materials showed by changing the content of carbon black. Then they were produced as sheets after pressing for 20 minutes at 180[$^{\circ}C$] with a pressure of 200[kg/cm$^{2}$]. The content of conductive carbon black was the variable, and their contents were 20, 30 and 40[wt$\%$], respectively. The modulus and tans were measured by DMA 2980. The ranges of measurement temperature were from -50[$^{\circ}C$] to 100[$^{\circ}C$] and measurement frequency was 1[Hz3. The modulus of specimens was increased according to a increment of a carbon black content. And modulus was rapidly decreased at the glass transition temperature. The tans of specimens was decreased according to a increment of a carbon black content. The smoothness was measured by JSM-6400. EEA resin from SEM measurement was best the dispersion of carbon back in base resin.

Keywords

References

  1. C. R. Anil Kumar, S. Deepa, A. K. Mishra and R. Sarathi,' Investigation into the failure of XLPE cables due to electrical treeing: a physico chemical approach', Polymer Testing, Vol. 22, No 3, pp. 313-318, 2003 https://doi.org/10.1016/S0142-9418(02)00106-X
  2. 한재홍, 김상준, 권오형, 강희태, 서광석, '반도전층내 불순물이 전력케이블의 신뢰도에 미치는 영향', 전기학회논문지, Vol.46, No.1, 1997
  3. 전용구, 김재경, 함덕순, 김진석, 'EVA의 Vinyl Acetate 함량변화에 따른 열적-기계적 성질 실험', Polymer (korea), Vol. 15, No. 4, pp. 402-410, 1991
  4. A. Marcilla, F. J. Sempere and J. A. Reyes-Labarta, 'Differential scanning calorimetry of mixtures of EVA and PE. Kinetic modeling', Polymer, Vol. 45, No. 14, pp. 4977-4985, 2004 https://doi.org/10.1016/j.polymer.2004.05.016
  5. A. Marcilla, J. A. Reyes-Labarta and F. J. Sempere, 'DSC kinetic study of the transitions involved in the thermal treatment of polymers. Methodological considerations', Polymer, Vol. 42, No. 12, pp. 5343-5350, June 2001 https://doi.org/10.1016/S0032-3861(00)00925-3
  6. 김성철 외, 고분자공학 I, 희중당, 1994, pp. 2-337
  7. M. Nafaa and H. Pavlos, 'Miscibility behaviour of ethylene vinylacetate/Novolac blends', Polymer, Vol. 36, No. 11, pp. 2165-2171, 1995 https://doi.org/10.1016/0032-3861
  8. S. L. Greene, ''Smoothness Evaluation of Clean Furnace Carbon Blacks', IEEE Electrical Insulation Magazine, Vol. 10, No.2, pp. 23-29, 1994 https://doi.org/10.1109/57.272901