Abstract
The degradation of IPA according to coating conditions was examined by $TiO_2/P-25-coated$ POF. In the photoactivity of $TiO_2-coated$ POF, ethanol solvent was higher activity than other solvents. Inorganic(KR-400), organic(A-9540) and inorganic$\cdot$organic hybrid(GPTMS, TMOS) resins were used as binder. Organic binder(A-9540) showed the highest activity for degradation of IPA, but organic binder was decomposed by $TiO_2$. Inorganic binder had lower binder ability than others, and lower adhesive than organic binders. In TMOS as inorganic · organic hybrid binder, activity of IPA degradation was decreased by addition of TMOS when the ratio of TMOS and P-25 was changed from 0.05 to 1.
본 연구에서는 광촉매 $TiO_2/P-25$를 POF에 코팅하여 IPA 분해 활성을 고찰한 결과, 코팅 시 용매의 조건은 에탄올에서 IPA의 분해효율이 가장 우수하였고 무기바인더(KR-400), 유기바인더(A-9540) 및 무$\cdot$유기 복합바인더(GPTMS, TMOS)중에서 유기 바인더인 A-9540을 사용했을 때 효율이 가장 우수한 것으로 나왔다. 유기 바인더는 광 분해반응에 의하여 바인더 자체가 분해되고 무기 바인더는 부착성이 떨어졌다. 유$\cdot$무기 복합 바인더 중에서 광분해 효율이 뛰어난 TMOS를 바인더로 선정하여 TMOS/P-25의 비율을 0.05부터 1로 바꾸어 광분해 실험을 수행한 결과, 바인더로써 TMOS의 첨가는 IPA분해 효율을 낮게 하였다.