Abstract
The $In_2S_3\;and\;In_2S_3:Co^{2+}$ thin films were grown by the spray Pyrolysis method. The thin films crystallized into tetragonal structures. The indirect energy band gap was 2.32ev for $In_2S_3\;and\;1.81eV\;for\;In_2S_3:Co^{2+}$ at 298K. The direct energy band gap was 2.67ev for $In_2S_3:Co^{2+}$ thin films. Impurity optical absorption peaks were observed for the $In_2S_3:Co^{2+}$ thin films. These impurity absorption peaks are assigned, based on the crystal field theory to the electron transitions between the energy levels of the $Co^{2+}$ ion sited in $T_{d}$ symmetry. The electrical conductivity($\sigma$), Hall mobility(${\mu}_H$), and carrier concentration (n) of the $In_2Se_3$ thin film were measured, and their temperature dependence was investigated.