Physical and Mechanical Properties of Phyllostachys pubescens Treated with Hot Water and Microwave Irradiation

열수 및 마이크로웨이브처리 맹종죽재의 물리적·기계적 특성

Phyllostachys pubescens planted in the Nambu Forest Experiment station in Jinju city of Gyongnam province was used, to investigate the physical and mechanical property of bamboo in this study. The ages of the P. pubescens were 1, 2 and 3 years, respectively. This experiment was carried out in August and January. The P. pubescens were divided into upper, middle and lower parts according to the growing points. The physical and mechanical properties of the P. pubescens were investigated before and after treatment of hot water and microwave irradiation. 1. The upper part of the P. pubescens indicated the highest static MOE according to the growing points. The range of the static MOE was from 70,000 to 110,000kgf/cm². 2. When P. pubescens were treated with hot water of 95℃, the ratio of softening was about 10~30%. 3. As microwave irradiation time was increased, the MOE values was decreased in both green and water-saturated bamboos. For the irradiation time of 20 and 30 seconds, the static MOE of P. pubescens was decreased up to about 50% comparing with non-treated.

열수 및 마이크로웨이브조사 처리가 벌채시기 및 부위별에 따른 맹종죽재의 물리적 기계적 특성을 평가하고, 효율적인 연화조건을 탐색하기 위하여 경남 진주시 가좌동에 위치한 남부임업시험장내에서 생육이 양호한 1, 2, 3년생의 죽재를 8월과 1월에 벌채하여 실험한 결과는 다음과 같았다. 1. 윗부위, 중간부위, 아랫부위의 부위별에 따른 휨탄성계수의 차이는 윗부위가 가장 높은 값을 나타내었고 중간부위, 아랫부위 순으로 낮은 값을 나타내었으며, 대부분이 70,000~110,000 kgf/cm²의 범위에 있었다. 2. 동적 탄성계수의 범위는 80,000~130,000 kgf/cm²의 범위로 정적 탄성계수보다 10-25% 정도 높게 나타났으며, 8월과 1월의 상관관계 R값이 각각 0.87과 0.68로 나타나 일반적인 목재와 같이 맹종죽재의 탄성계수 측정에도 비파괴 방법인 양단자유진동에 의해서도 예측 가능하였다. 3. 95℃의 열수로 처리했을 때 연화율은 10~30%를 나타내었다.4. 생재 및 포수 두 조건 모두 마이크로웨이브조사 처리 시간이 길어질수록 탄성계수가 낮아졌으며, 20초 및 30초간 처리했을 때 생재 휨탄성계수의 약 50% 이하로 떨어져 생재를 20초간 마이크로웨이브조사 처리했을 때가 본 연구에서 죽재를 연화시키는데 가장 효과적인 방법이었다.