The Shear Resistance of Rc Deep Beam with Web Opening Repaired and Reinforced by Fiber Sheets After Shear Failure

깊이가 큰 철근콘크리트 유공보의 보수·보강 전후의 내력에 관한 연구

In this study, deep beam specimens are designed to have the effective shear span to depth ratio 1.0 and web opening within effective shear region. The purpose of this study is to investigate experimentally the shear strengthening effect between before failure and after failure upon using fiber sheets for RC deep beam with opening in web. The results can be summarized as follows; 1)When deep beams with web opening were failed in shear, their initial diagonal crack load and crack width were not influenced by their types of the arranged steel bars. 2)Deep beam with the horizontal reinforced bar was effective in the ultimate load of deep beam with web opening in shear failure 3)There were the approximate values between the experimental values and the analysis of finite element method. 4)The ultimate failure strengths of the repaired and strengthened specimens were increased about 34.4%~83.8% in comparison with specimens not to be strengthened.

본 연구는 유효전단스팬에 대한 깊이의 비가 1.0인 깊이가 큰 보에 대해서 유효전단영역내에 개구부에 대한 파괴 메카니즘의 변화와 전단파괴된 후 보수 보강에 따른 부재 내력의 복원력에 관한 연구로서, 그 결론는, 전단파괴한 유공보 시험체의 초기사균열 하중은 시험체 간에 큰 차이가 없어 시험체의 배근형태에 영향을 받지 않는 것으로 나타났으며, 아라미드 시트로 보강된 시험체의 균열 및 파괴형태는 중앙부의 휨 균열과 전단지간의 사균열이 동시에 발생한 후, 최대내력근처에서 유공측의 전단균열이 확대되어, 시트면의 중앙부위가 박리되면서 전단파괴 되었다. 전단파괴된 깊이가 큰 보 시험체를 아라미드 섬유시트로 보강한 결과 보강전과 비교하여 최대내력은 최소 34.4%, 최대 83.8%의 증가를 나타내어 파괴전의 내력을 복원하는 것으로 나타났다.