Resources Recycling (자원리싸이클링)

The Korean Institute of Resources Recycling (한국자원리싸이클링학회)
권호 표지

Studies on Preparation of Transparent Iron Oxide

투명산화철의 製造에 관한 硏究

  • Baek, Moo-Hyun (Dept. of Metallurgical Eng., Chungnam National University) ;
  • Lim, Jong-Ho (Dept. of Metallurgical Eng., Chungnam National University) ;
  • Kim, Tae-Kyung (Dept. of Metallurgical Eng., Chungnam National University) ;
  • Lee, Seoung-Won (Dept. of Metallurgical Eng., Chungnam National University)
  • 백무현 (충남대학교 금속공학과) ;
  • 임종호 (충남대학교 금속공학과) ;
  • 김태경 (충남대학교 금속공학과) ;
  • 이승원 (충남대학교 금속공학과)
  • Published : 2004.12.01
Download PDF
⟨ Previous Next ⟩

Abstract

The optimum conditions were studied for the preparation of transparent iron oxide with the air oxidation of FeOOH. The FeOOH obtained by mixing NaOH and FeSO$_4$ solution in various conditions such as R(=2NaOH/FeSO$_4$), FeSO$_4$ concentration. reaction temperature and air flow rate. When the FeSO$_4$ increased gradually, the concentration of iron ion in the solution became high. So, particle size increased precipitating Fe$_3O_4$. Goethite dehydrate at about 200$^{\circ}C$ and ended the reaction at about 320$^{\circ}C$ forming hematite. The lower the reaction temperature was, the shorter the particle length of goethite and particle size decreased. When the flow rate of air as an oxidant increased, the amount of dissolved oxygen in the solution increased, which made oxidation rate increased. And then particle size of goethite decreased.

FeSO$_4$ 용액에 NaOH를 첨가하여 FeOOH를 제조하였으며, R(=2NaOH/FeSO$_4$), FeSO$_4$의 농도, 반응온도 및 산화용 가스인 air의 유량 변화에 따른 제조변수를 통해 투명산화철의 제조 조건을 연구하였다. 수용액 중에 FeSO$_4$의 농도가 증가할수록 Fe$_3O_4$를 석출하며 입자의 크기가 증가하였다. 생성된 FeOOH는 약 200$^{\circ}C$에서 탈수반응을 일으켜 약 320$^{\circ}C$부근에서 종료하였다. 반응온도가 낮을수록 Fe(OH)$_2$의 입자의 길이가 짧아졌으며, 산화제인 air의 공급량이 클수록 용액 중에 용존산소의 량이 증가하여 Fe(OH)$_2$의 입자길이가 감소하였다.

Keywords

References

  1. 손진군, 김대영, 이재영, 이훈하, 2002: 산화철 안료의 색상개선 연구, 자원리사이클링학회지, 11(5), pp. 24-29
  2. 성주경, 설수덕, 황용길, 1975: 황산제일철로부터 함수산화 철생성에 관한 연구, 대한화학회지, 19(2), pp. 142-146
  3. Tsuruta, E., 1998: Industrial Heritage of the Wakasa Iron Oxide, J. of the Jap. Soc of colour Mat., 71(6) pp.375-382 https://doi.org/10.4011/shikizai1937.71.375
  4. Nishio, A., 1998: Fine Powder of Mixed Metal Oxide Pigments, J. of the Jap. Soc of colour Mat., 71(6) pp.398-404 https://doi.org/10.4011/shikizai1937.71.398
  5. 손진군, 변태봉, 이재영, 김대영, 1996: 철강산업발생 폐산세액 재활용을 위한 불순물 제거 연구, 한국자원리싸이클링학회지, 5(2), pp. 57-62
  6. Yogo, T., Nakamura, T., Sakamoto, W., Hirano. S., 2000: Synthesis of Transparent Magnetic Particle/Organic Hybrid film using Iron-Organics, J. of Mater. Res., 15(10) pp. 2114-2121 https://doi.org/10.1557/JMR.2000.0304
  7. Peter Wright., 2002: Transparent Iron Oxide Pigments for Wood-Coating Application, Intertech Conf. 20-22 March. Releigh North Carolina, Printed in U.S.A
  8. 오재현, 김주호, 염남기, 김문수, 1987: 자황철광의 이용에 관한 연구-자황철광의 침출액으로부터 $\alpha$-Fe$_2$O$_3$의 합성, 한국자원공학회지, 24(2) pp. 135-144
  9. 오재현, 이시형, 강남기, 김만, 1993: 습식법에 의한 자기 기록용 자성분말의 제조 및 특성에 관한 연구(수용액중에서 게사이트의 합성 및 물성에 관하여), 대한금속재료학회지, 31(10) pp. 1345-1354
  10. 조성걸, 1985: Influences of Transition Metal Iron on the Shape and Magnetic Property of Acicular Magnetic Iron Oxide, 서울대학교대학원 석사학위 논문, 서울, 한국
  11. 황용길, 성주경, 김재호, 1974: 피클링 폐황산으로부터 안료의 제조, 한국금속학회지, 12(2) pp. 122-126
  12. Kiyarna, M., 1974: Conditions for the Formation of Fe$_3$O$_4$ by the Air Oxidation of Fe(OH)$_2$ Suspension, Bull. Chem. Soc. Jap., 47(7) pp. 1646-1650 https://doi.org/10.1246/bcsj.47.1646
  13. 변태봉, 이재영, 김대영, 손진군, 권순주, 1991: 산세페액을 이용한 Maghemite의 제조 한국세라믹학회지, 28(12) pp. 996-1004