Effect of Stabilization Processing Conditions on the Thermal Shrinkage and the Thermal Stability of Rayon Fabrics Untreated and Surface-Treated with Phosphoric Acid

인산처리 유·무에 따른 레이온직물의 열수축과 열안정성에 미치는 안정화 공정 조건의 영향

We investigated the effect of stabilization processing parameters on the thermal shrinkage, thermal stability and microstructure of rayon fabrics stabilized under various conditions such as heating rate, stabilization temperature, atmosphere gas, and chemical treatment. The presence and absence of phosphoric acid treatment and the heating rate have most importantly influenced the thermal shrinkage and the weight change of rayon fabrics. Especially, the phosphoric acid treatment decreases the reduction of thickness, length, and weight of the fabrics by about 80%, 20%, and 26%, respectively, in comparison with the untreated counterparts, showing the protective effectiveness of the thermal shrinkage involved. The thermal stability of stabilized rayon fabrics is also affected by all the processing conditions used: stabilization temperature, phosphoric acid treatment, atmosphere gas, and heating rate. In addition, the surface and diameter of the stabilized fiber significantly depend on the treatment of phosphoric acid prior to stabilization process.

본 연구에서는 레이온직물에 대하여 승온속도, 안정화온도, 분위기가스, 화학적 표면처리 등 여러가지 조건에서 안정화공정을 행한 후, 직물의 열수축과 열안정성, 그리고 미세구조에 미치는 공정 조건의 영향을 조사하였다. 레이온직물의 열수축과 중량변화에 인산처리 유무와 승온속도가 가장 중요한 영향을 미쳤다. 특히, 인산처리를 한 경우가 하지 않은 경우보다 레이온직물의 두께변화는 약 80%, 길이변화는 약 20%, 그리고 중량변화는 약 26%가 줄어드는 열수축 억제 효과를 보여주었다. 안정화 된 레이온직물의 열안정성에는 안정화온도와 인산처리 그리고 분위기가스와 승온속도 등 주어진 안정화공정 조건 모두가 영향을 주었다. 또한 안정화섬유의 표면 상태 및 섬유직경 변화도 공정 전에 행한 인산처리의 유무에 의존하였다.