Analytical model of corrosion-induced cracking of concrete considering the stiffness of reinforcement

  • Bhargava, Kapilesh (Bhabha Atomic Research Center) ;
  • Ghosh, A.K. (Bhabha Atomic Research Center) ;
  • Mori, Yasuhiro (Graduate School of Environmental Studies, Nagoya University) ;
  • Ramanujam, S. (Bhabha Atomic Research Center)
  • 투고 : 2003.03.13
  • 심사 : 2003.09.02
  • 발행 : 2003.12.25

초록

The structural deterioration of concrete structures due to reinforcement corrosion is a major worldwide problem. Service life of the age-degraded concrete structures is governed by the protective action provided by the cover concrete against the susceptibility of the reinforcement to the corrosive environment. The corrosion of steel would result in the various corrosion products, which depending on the level of the oxidation may have much greater volume than the original iron that gets consumed by the process of corrosion. This volume expansion would be responsible for exerting the expansive radial pressure at the steel-concrete interface resulting in the development of hoop tensile stresses in the surrounding cover concrete. Once the maximum hoop tensile stress exceeds the tensile strength of the concrete, cracking of cover concrete would take place. The cracking begins at the steel-concrete interface and propagates outwards and eventually resulting in the through cracking of the cover concrete. The cover cracking would indicate the loss of the service life for the corrosion-affected structures. In the present paper, analytical models have been developed considering the residual strength of the cracked concrete and the stiffness provided by the combination of the reinforcement and expansive corrosion products. The problem is modeled as a boundary value problem and the governing equations are expressed in terms of the radial displacement. The analytical solutions are presented considering a simple 2-zone model for the cover concrete viz. cracked or uncracked. A sensitivity analysis has also been carried out to show the influence of the various parameters of the proposed models. The time to cover cracking is found to be function of initial material properties of the cover concrete and reinforcement plus corrosion products combine, type of rust products, rate of corrosion and the residual strength of the cover concrete. The calculated cracking times are correlated against the published experimental and analytical reference data.

키워드

참고문헌

  1. ACI 318 (1985), Standard Code Requirements for Reinforced Concrete and Commentary, American Concrete Institute, Detroit, USA.
  2. Andrade, C., Alonso, C. and Molina, F.J. (1993), "Cover cracking as a function of rebar corrosion : part Iexperimental test", J. Mat. and Struct., Paris, 26, 453-464. https://doi.org/10.1007/BF02472805
  3. Bazant, Z.P. (1979a), "Physical model for steel corrosion in sea structures - theory", J. Struct. Div., ASCE, 105(6), 1137-1153.
  4. Bazant, Z.P. (1979b), "Physical model for steel corrosion in sea structures - applications", J. Struct. Div., ASCE, 105(6), 1155-1166.
  5. Cady, P.D. and Weyers, R.E. (1984), "Deterioration rates of concrete bridge decks", J. Transportation Engg., 110(1), 34-45. https://doi.org/10.1061/(ASCE)0733-947X(1984)110:1(34)
  6. CEB-FIP (1990), Comite Euro-International du Beton-Federation International de la Precontrainte - Design Code, Thomas Telford, London, UK.
  7. IS 456 (2000), Indian Standard Code of Practice for Plain and Reinforced Concrete, 4th Revision, Bureau of Indian Standards, New Delhi, INDIA.
  8. Liu, Y. and Weyers, R.E. (1998), "Modelling the time-to-corrosion cracking in chloride contaminated reinforced concrete structures", ACI Mat. J., 95(6), 675-681.
  9. Martin-Perez, B. (1998), "Service life modeling of RC highway structures exposed to chlorides", Ph.D. Dissertation, Dept. of Civil Engineering, University of Toronto, Toronto.
  10. Mehta P.K. and Monteiro, Paulo J.M. (1997), Concrete Microstructure, Properties and Materials, 1st Ed., Indian Concrete Institute, Chennai, India.
  11. Morinaga, S. (1989), "Prediction of service lives of reinforced concrete buildings based on the rate of corrosion of reinforcing steel", Special report of the Institute of Technology, Skimiza Corporation, JAPAN.
  12. Pantazopoulou, S. and Papoulia, K.D. (2001), "Modeling cover-cracking due to reinforcement corrosion in RC structures", J. Struct. Div., ASCE, 127(4), 342-351.
  13. Rasheeduzzafar, Al-Saadoun, S.S. and Al-Gahtani, A.S. (1992), "Corrosion cracking in relation to bar diameter, cover and concrete quality", J. Mat. Civ. Eng., ASCE, 4(4), 327-343. https://doi.org/10.1061/(ASCE)0899-1561(1992)4:4(327)
  14. Timoshenko, S.P. and Goodier, J.N. (1970), Theory of Elasticity, 3rd Ed., McGraw-Hill Book Company, New York, USA.

피인용 문헌

  1. Non-uniform time-to-corrosion initiation in steel reinforced concrete under chloride environment vol.82, 2014, https://doi.org/10.1016/j.corsci.2014.01.023
  2. Comparison of uniform and non-uniform corrosion induced damage in reinforced concrete based on a Gaussian description of the corrosion layer vol.53, pp.9, 2011, https://doi.org/10.1016/j.corsci.2011.05.017
  3. Safety assessment of in-service reinforced concrete T-girders of bridge decks vol.18, pp.5, 2017, https://doi.org/10.1002/suco.201600162
  4. Degradation of flexural strength in reinforced concrete members caused by steel corrosion vol.54, 2014, https://doi.org/10.1016/j.conbuildmat.2013.12.101
  5. Model for cover cracking due to rebar corrosion in RC structures vol.28, pp.8, 2006, https://doi.org/10.1016/j.engstruct.2005.11.014
  6. Time-dependent reliability of corrosion-affected RC beams—Part 1: Estimation of time-dependent strengths and associated variability vol.241, pp.5, 2011, https://doi.org/10.1016/j.nucengdes.2011.01.005
  7. Ultimate flexural and shear capacity of concrete beams with corroded reinforcement vol.27, pp.3, 2007, https://doi.org/10.12989/sem.2007.27.3.347
  8. Estimation of transfer lengths in precast pretensioned concrete members based on a modified thick-walled cylinder model vol.17, pp.1, 2016, https://doi.org/10.1002/suco.201500049
  9. A comparative study on factors affecting time to cover cracking as a service life indicator vol.163, 2018, https://doi.org/10.1016/j.conbuildmat.2017.12.120
  10. Factors Affecting Life-Cycle Cost Analysis of RC Structures in Chloride Contaminated Environments vol.13, pp.2, 2007, https://doi.org/10.1061/(ASCE)1076-0342(2007)13:2(135)
  11. Cover cracking of reinforced concrete due to rebar corrosion induced by chloride penetration vol.41, pp.8, 2011, https://doi.org/10.1016/j.cemconres.2011.04.008
  12. A double-cylinder model incorporating confinement effects for the analysis of corrosion-caused cover cracking in reinforced concrete structures vol.99, 2015, https://doi.org/10.1016/j.corsci.2015.07.009
  13. Modelling of corrosion-induced cover cracking in reinforced concrete by an embedded cohesive crack finite element vol.93, 2012, https://doi.org/10.1016/j.engfracmech.2012.06.010
  14. Analytical model for time to cover cracking in RC structures due to rebar corrosion vol.236, pp.11, 2006, https://doi.org/10.1016/j.nucengdes.2005.10.011
  15. Probabilistic Lifetime Assessment of RC Pipe Piles Subjected to Chloride Environments vol.30, pp.11, 2018, https://doi.org/10.1061/(ASCE)MT.1943-5533.0002512
  16. Space-time Gaussian models for evaluating corrosion-induced damages in reinforcing bars vol.44, pp.1, 2019, https://doi.org/10.1007/s12046-018-1015-7
  17. A method of global-local analyses of structures involving local heterogeneities and propagating cracks vol.38, pp.4, 2011, https://doi.org/10.12989/sem.2011.38.4.529
  18. Reliability analysis of laterally loaded piles in marine environments considering the degradation of flexural rigidity vol.39, pp.11, 2021, https://doi.org/10.1080/1064119x.2020.1839825