Abstract
The change of microstructures in the base metal during transient liquid phase bonding process of directionally Ni base superalloy, GID-111 was investigated. Bonds were fabricated using a series of holding times(0~7.2ks) at three different temperatures. The flip chip bonding utilizing self-aligning characteristic of solder becomes mandatory to meet tolerances for the optical device. In this paper, a parametric study of aging condition and pad size of samples was evaluated. A TiW/Cu/electroplated Cu UBM structure was selected and the samples were aging treated to analyze the effect of intermetallic compounds with the time variations. An FIB technique was applied to the preparation of samples for TEM observations. An FIB technique is very useful to prepare TEM thin foil specimens from the solder joint interface. After aging treatment, the tendency to decrease in shear strength was measured and the structure of the solder and the UBM was observed by using SEM, TEM and EDS. As a result, the shear strength was decreased of about 21% in the 100${\mu}{\textrm}{m}$ sample at 17$0^{\circ}C$ aging compared with the maximum shear strength of the sample with the same pad size. In the case of the 12$0^{\circ}C$ aging treatment, 18% of decrease in shear strength was measured at the 100${\mu}{\textrm}{m}$ pad size sample. An intermetallic compound of Cu6Sn5 and Cu3Sn were also observed through the TEM measurement by using.