Abstract
A method was investigated to determine the thickness of coating on steel sheet using rf glow discharge atomic emission spectrometer. The RF gas-jet boosted glow discharge has such salient feature as good pleasure stability and high sputtering efficiency that it was possible to determine the thickness of silicon resin film on zinc electroplated steel. The erosion speed variation is dependent on discharge power, gas flow rate and discharge pressure. therefore determine discharge condition to measure the thickness of coating on steels. The fundamental studies have been carried out to investigate an optimum condition for in-depth analysis and composition of zinc coating on steel. In this study, the calibration curve for thickness determination of silicon resin film was found to be linear in the range of $1000{\sim}3500mg/m^2$ film thickness. The developed rf gas-jet boosted glow discharge was applied to the analysis of zinc coating and silicon resin film on steel made by RIST.
RF 글로우 방전 원자 방출 분광법을 사용하여 다층 도금강판 두께분석을 하였다. 일반적으로 gas jet boosted 글로우 방전은 플라스마 안정성과 스퍼터링 효율이 우수하여 기존의 두께 분석법에서 측정이 어려운 다층 두께분석이 가능하며, RF를 사용하여 비전도성 실리콘-수지계열의 다층 도금강판 두께분석이 가능하였다. RF gas-jet boosted 글로우 방전은 방전전원과 가스 흐름량 그리고 방전압력에 의해 스퍼터링을 조절할 수 있다. 그래서 스퍼터링 효율에 의해 다층 도금된 강판의 경우 소재에 따라 서로 다른 조건에서 측정할 수가 있었다. 본 연구에서 두께 $20{\mu}m$의 아연층을 가진 아연 도금강판의 두께 및 조성을 분석하기 위해서 최적조건에 대한 연구를 하였고, 두 가지 기준물질로 구성된 수지 도금강판을 이용해서 검량선을 측정하였다. 본 연구에 최적조건 및 검량을 하기 위해서 아연합금 도금강판 및 실리콘-수지 도금강판은 포항 산업 과학 기술원(RIST)에서 제공하였다.