Abstract
For the experimental study of rotor steel, seven kind of specimens with different degradation levels were prepared by isothermal heat treatment at $630^{\circ}C$. Spherical indentation technique was developed to evaluate the flow properties of metallic materials in carbon steel, stainless steel, and alloys, etc. Through the spherical indentation test, differently degraded 1Cr-1Mo-0.25V steel's mechanical properties were observed and compared with conventional standard test data. The flow properties of 1Cr-1Mo-0.25V steel's were estimated by analyzing the indentation load-depth curve. To characterize the flow property, we used material yield slope and constraint factor index rather than strain-hardening exponent because the variation of strain-hardening exponent was very little and the data showed irregularly. And the constraint factor's effect was small when the material yield slope was taken into account.
발전소의 터빈 로터강의 수명을 평가하기 위하여 $630^{\circ}C$에서 등온 열처리된 7가지의 서로 다른 시편을 준비하였다. 탄소강, 스테인레스강 등의 금속재료의 유동특성을 평가하기 위하여 개발된 구형압입 시험을 통하여 서로 다르게 열화된 1Cr-1Mo-0.25V강의 기계적 물성을 측정하고 이를 인장시험에서의 결과와 비교하였다. 유동특성을 결정짓는 요소로 재료항복기울기와 구속인자지수를 사용하였다. 이는 가공경화지수의 변화가 매우 작고 불규칙적으로 나타났기 때문이다. 또한 재료항복기울기의 영향을 고려하였을 때 구속인자지수의 영향은 적은 것으로 나타났다.