Antistatic Behavior of UV-curable Multilayer Coating Containing Organic and Inorganic Conducting Materials

유·무기 전도성 물질을 함유한 UV 경화형 다층 코팅의 대전방지 특성

  • Kim, Hwa-Suk (Dept. of polymer science & Eng., Chosun University) ;
  • Kim, Hyun-Kyoung (Dept. of polymer science & Eng., Chosun University) ;
  • Kim, Yang-Bae (Institute of Photonics & Surface Treatment, Q-Sys Co., Ltd.) ;
  • Hong, Jin-Who (Dept. of polymer science & Eng., Chosun University)
  • 김화숙 (조선대학교 공과대학 고분자공학과) ;
  • 김현경 (조선대학교 공과대학 고분자공학과) ;
  • 김양배 ((주)큐시스) ;
  • 홍진후 (조선대학교 공과대학 고분자공학과)
  • Received : 2002.07.15
  • Accepted : 2002.09.03
  • Published : 2002.09.23
Download PDF
⟨ Previous Next ⟩

Abstract

UV curable coating system described here consists of double layers, namely under layer and top laser coatings. The former consists of organic-inorganic conductive materials and the latter consists of multifunctional acrylates. Transparent double layer coatings were prepared on the transparent substrates i.e. PMMA, PC, PET etc. by the wet and wet coating procedure. Their surface resistances and film properties were measured as a function of the top layer thickness and relative humidity. As the thickness of the top layer was less than $10{\mu}m$, the surface resistance in the range of $10^8{\sim}10^{10}{\Omega}/cm^2$ was obtained. The surface properties of the two-layer coating were remarkably improved compared with the single layer coating. The effects of migration of conducting materials on the film properties of multilayer coating were investigated by using contact angle and Fourier transform infrared/attenuated total reflection(FT-IR/ATR). It was found that the migration of dopant(dodecyl benzenesulfonic acid, DBSA) molecules were occurred from film-substrate interface to film-air interface in the organic conductive coating system but not in the inorganic one.

하층에 유 무기 전도성 물질을 코팅하고 상층은 다관능성 아크릴레이트를 코팅한 다층코팅의 자외선 경화형 시스템을 도입하였다. 이러한 다층코팅은 투명한 PMMA, PC, PET 등의 기재 위에 wet and wet 방식의 코팅 방법을 사용하여 제조하였다. 도막의 표면저항과 물성은 상층 두께의 변화와 상대 습도를 다르게 하여 측정하였다. 상층두께가 $10{\mu}m$ 이하일 때 $10^8{\sim}10^{10}{\Omega}/cm^2$의 표면저항을 나타냈으며 표면 물성은 단층코팅에 비해서 다층코팅이 더 우수하게 나타났다. 그리고 다층코팅에서의 도판트 이동효과는 접촉각과 FT-IR/ATR을 통해 관찰하였다. 하층이 무기 전도성 물질인 경우에는 관찰되지 않는 도판트(DBSA)의 필름-기재 계면에서 필름-공기 계면 쪽으로 이행되는 거동이 유기전도성 물질인 경우에는 관찰되었다.