Abstract
Low temperature sintering of Co$_2$Z type Ba ferrites with various oxide additives has been studied. Co$_2$Z phase was obtained by 2 step calcination and XRD peaks showed a good agreement with the peaks of the standard Co$_2$Z phase, except for some minor extra peaks. ZnO-B$_2$O$_3$ glass, ZnO-B$_2$O$_3$ and CuO, ZnO-B$_2$O$_3$ and Bi$_2$O$_3$, and ZnO-Bi$_2$O$_3$ glass were added to lower sintering temperatures. Specimens were sintered at the temperature range between 900 $^{\circ}C$ and 1000 $^{\circ}C$. In the single addition of ZnO-B$_2$O$_3$ glass, the specimen with 7.5 wt% showed the highest shrinkage. Specimens with complex addition of ZnO-B$_2$O$_3$ glass with CuO or Bi$_2$O$_3$ showed higher shrinkages and initial permeabilities than single addition of ZnO-B$_2$O$_3$ glass. Shrinkages and initial permeabilities of the specimens with ZnO-Bi$_2$O$_3$ glass were higher than those of ZnO-B$_2$O$_3$ glass addition.
각종 산화물을 첨가하여 Co$_2$Z type Ba-ferrite의 저온소결에 관하여 연구하였다. Co$_2$Z type Ba-ferrite 상은 2회 하소과정을 통하여 얻을 수 있었으며, 생성된 상의 XRD peaks는 일부 minor peaks 제외하고는 standard peaks와 거의 일치하였다 제조된 분말은 저온소결을 위하여 ZnO-B$_2$O$_3$ glass리 단독 첨가 및 CuO 또는 Bi$_2$O$_3$와 복합 첨가하였으며, 또한 ZnO-Bi$_2$O$_3$ glass를 단독 첨가하였다. 소결은 900~100$0^{\circ}C$에서 수행하였다. ZnO-B$_2$O$_3$ glass의 단독 첨가 시, 첨가량이 7.5 wt%일 때 가장 높은 수축거동을 나타내었다. ZnO-Bi$_2$O$_3$ glass와 CuO 또는 Bi$_2$O$_3$를 복합 첨가하였을 때, glass를 단독 첨가하였을 경우보다 수축률이 급격히 증가되었다. 또한 ZnO-Bi$_2$O$_3$ glass를 단독 첨가한 시편의 수축률과 초기 투자율은 ZnO-B$_2$O$_3$ glass를 단독 첨가한 시편보다 높은 값을 나타내었다.