Photodarkening and Thermal Bleaching Effect in Ge-doped Multicomponent Oxide Glasses by UV Irradiation

자외선 조사에 따른 게르마늄 함유 다성분계 산화물 유리의 광흑화와 열표백화 현상

Ge-doped rnulticomponent oxide glasses were prepared by a conventional melting method. The change of micro structure in glasses was investigated by using PL (photoluminescence) and ESR (electron spin resonance). Before UV irradiation, the PL intensity increased according to germanium contents, but decreased the intensity as soon as UV irradiation. A changed property was recovered near it original properties when it was annealed. These photodarkening and thermal bleaching effect were observed by ESR intrument. These effect did not change the glass phase but vary only change of micro structure.

게르마늄첨가 다성분계 산화물 유리를 제조하여 자외선(UV) 조사에 따른 유리의 미세 구조변화를 PL(photo-luminescence)과 ESR(electron spin resonance)을 이용하여 관찰하였다. 게르마늄 첨가량이 증가함에 따라 PL방사량은 증가하였으며, UV 조사 후에는 처음과 반대되는 광혹화 현상으로 감소하는 현상을 나타냈다. UV조사로 변화된 특성은 열처리를 통하여 회복이 가능하였으며, ESR 측정에서도 PL결과와 같은 광혹화 현상(phodarkenine effect)과 열표백화 현상(thermal bleaching effect)이 확인되었다. 또한, XRD 분석을 통하여 이러한 현상이 비정질 상은 그대로 유지하는 미세구조 변화임을 알 수 있었다.