Abstract
Small diameter composite helical springs (CS) are developed using a hot plated mold for reinforcement of common optical fiber jumper cord (OJC). The outer diameters of the springs are about 2 ~ 3mm. These springs are inserted into the OJC to protect the damage of an optical fiber from the sudden lateral load. Two types of CS, Yarn type (Y-type) and Band type (B-type), are manufactured to compare the effectiveness for the damage protection. The experimental works were conducted to check the effect of the CS covered around OJC on the mechanical and optical properties. Experimental observations show a considerable effect on the flexural resistance, hence slowing down the deterioration of the optical power by the internal damage of the fiber. Obtained main results are as follows: (1) Y-type CS has better protection abilities to lateral loading than B-types. (2) Compared with bare OJC, CS-OJC has less power loss under the loading. (3) OJC covered with the composite coil spring has a possibility for a practical usage with full fruits.
미세 직경을 갖는 복합재료 나선형 스프링 (CS)가 광점퍼코드 (OJC)를 보강하기위한 매체로써 개발되었다. 이 스프링의 외경은 약 2~3mm로써 광점퍼코드에 갑작스런 측면 하중으로 부터 광섬유의 손실을 막기위해 삽입 보강할 수 있도록 제작되었다. 섬유 형태 (Y-type)와 밴드 형태 (B-type)의 복합재료 스프링이 제작되어 그 효과를 비교하였다. 측면 하중에 대한 기계적 특성은 동일 직경의 금속 스프링 및 일반 광점퍼코드의 물성치와 비교하여 제시하였다. 실험 결과로부터 복합재료 스프링이 보강된 광점퍼코드의 경우 굽힘에 대한 높은 저항력을 지니고 있음에 따라 광섬유의 내부 손상에 의한 광 손실의 감소률이 낮음을 알 수 있었다 얻어진 주요 결과들은: (1) Y-type의 CS의 경우 B-type과 비교하여 높은 측압 저항력을 지님을 알 수 있었다 (2) 일반 OJC와 비교하여 CS-OJC의 경우 광 손실이 현격이 낮음을 알 수 있었다. (3) 일반 스프링의 측압 하중시의 응력 분포 형태를 제시하였으며. 실험으로부터 얻어진 결과로부터 복합재료 스프링이 보강된 광점퍼 코드의 경우 매우 높은 구조적 안정성을 보임을 알 수 있었다.