Effect of Hydrogen in ITO(Indium Tin Oxide) Thin Films Etching by Low Temperature Plasma at Atmospheric Pressure

대기압 저온 플라스마에 의한 ITO(Indium Tin Oxide)박막 식각의 수소(H$_2$)효과

  • Lee, Bong-Ju (Dept.of Physics Chemistry, Chosun University)
  • 이봉주 (조선대학교 물리화학부)
  • Published : 2002.08.01

Abstract

It is confirmed that the ITO(Indium Tin Oxide) thin films can be etched by low-temperature plasma at atmospheric pressure. The etching happened deepest at a hydrogen flow rate of 4 sccm, and the etch rate was 120 /min. The etching speed corresponded to the H$\alpha$* emission intensity The etching mechanism of the ITO thin films is as follows; thin films were reduced by H$\alpha$*, and the metal compound residues were detached from the substrate by reacting on the CH* The etching was started after etching time of initial 50 sec and above the threshold temperature of 145$^{\circ}C$. The activation energy of 0.16 eV(3.75 Kcal/mole) was obtained from the Arrehenius plots.

산화인듐(ITO)박막은 대기압 저온 플라스마에 의해 식각이 가능하다는 것을 확인했다. 식각은 수소유량 4 sccm에서 가장 깊게 발생하여, 120 /min를 나타내었다. 식각속도는 Hα*의 발광강도와 대응하였다. ITO박막의 식각 메커니즘은 Hα*에 의해 환원이 된후, 남게 된 금속 화합물은 CH*과 반응하여 기판으로부터 이탈한다고 생각된다. 식각은 식각시간 50초 이상에서부터, 기판온도 145℃ 이상부터 발생하기 시작하였다. 활성화 에너지는 Arrehenius plots으로부터 0.16eV(3.75kcal/mole)를 얻었다

Keywords

References

  1. C. T. Hsu, J. W. Li, C. H. Liu, Y. K. Su, T. S. Wu and M. Yokoyama, 'High luminous efficiency thin-film electroluminescent devices with low resistivity insulating materials', J. Appl. Phys. Vol. 71, No. 3, pp. 1509-1512, 1992 https://doi.org/10.1063/1.351219
  2. J. W. Li, Y. K. Su and M.Yokoyama, 'The constructions and optical characteristics of multi-color or full-color ACTFEL desplay devices', J. Electro. Mater. Vol. 21, No. 6, pp. 659-665, 1992 https://doi.org/10.1007/BF02655436
  3. C. T. Hsu, Y.J. Liu, J. W. Li, Y. K. Suand M. Yokoyama, 'Crystallinity of ZnS:Tb,F thin films and characteristics of green-color thin-film electroluminescent devices by rf-magnetron sputtering', J. Appl. Phys, Vol. 72, No. 10, pp. 4655-4659, 1992 https://doi.org/10.1063/1.352121
  4. R. J. Saia, R. F. Kwasnick and C. Y. Wei, 'Selective reactive ion etching of indiun-Tin Oxide in Hydrocarbon gas mixture', J. Electrochem. Sci. Vol. 138, No. 2, pp. 493-496, 1991 https://doi.org/10.1149/1.2085616
  5. Z. Calahorra, E. Minami, R. M. White and R. S. Muller, 'Reactive ion etching of Indiun-Tin Oxide films', J. Electrochem. Sci. Vol. 136, No. 6, pp. 1839-1840, 1989 https://doi.org/10.1149/1.2097042
  6. M. Mohri, H. Kakinurma, M. Sakamoto and H. Sawai, 'Plasma etching of ITO thin films using a $CH_4/H_4$ gas mixture', Jpn. J. Appl. Phys. Vol. 29, No. 10, pp. L1932-L1935, 1990 https://doi.org/10.1143/JJAP.29.L1932
  7. I. Adesida, D. G. Ballegeer, J. W. Seo, A. Ketterson, H. Chang and K. Y. Cheng, 'Etching of Indium Tin Oxide in Methane/hydrogen plasma', J. Vac. Sci. & Technol. B9, No. 6, pp. 3551-3554, 1991
  8. C. haag and H. Suhr, 'Etching of metal by means of organic radical', Plama Chem. Plasma pressing. Vol. 6, No. 3, pp. 197-203, 1986 https://doi.org/10.1007/BF00575128
  9. H. Koinuma, H. Ohkubo, T. Hashimoto, K. Inomata, T. Shiraishi, A. Miyanaga and S. Hayashi, 'Development and application of microbeam plasma generator', Appl. Phys. Lett. Vol. 60, No. 7, pp. 816-817, 1992 https://doi.org/10.1063/1.106527
  10. Bong Ju Lee, Yukihiro Kusano, Nobuko Kato, Kazuo Naito, Takao Horiuch and Hideomi Koinuma, 'Oxygen Plasma Treatment of Rubber Surface by the Atmospheric Pressure Cold Plasma Torch', Jpn. J. Appl. Phys. Vol. 36, No. 5A, pp. L2888-L2891, 1997 https://doi.org/10.1143/JJAP.36.2888
  11. K. J. Clay, S. P. Speakman, G. A. J. Amaratunga and S. R. P. Silva, 'Characterization of a-C:H:N deposition from $CH_4/N_2$ rf Plasma using Optics emission Spectroscopy', J. Appl. Phys. Vol. 79, No. 9, pp. 7227-7233, 1996 https://doi.org/10.1063/1.361439
  12. J. Appl. Phys. v.79 no.9 Characterization of a-C:H:N deposition from CH₄/N₂rf Plasma using Optics emission Spectroscopy K.J.Clay;S.P.Speakman;G.A.J.Amaratunga;S.R.P.Silva https://doi.org/10.1063/1.361439