A Study on Examination of Application in Waste Filled Land and Performance Evaluation as Waterproofing Material by the Spray Water-Soluble Rubber Asphalt

뿜칠형 수용성 고무화 아스팔트 차수재의 성능평가 및 폐기물 매립지 적용성 검토에 관한 연구

This study examinated the application in construction field and the development of waterproofing material system by the spray water-soluble rubber asphalt to solve the problems of synthetic polymer sheet and gio membrane(A mat sheet of Bentonite) that had been used domestic waterproofing material in advance. As the result of study, characters of study water-soluble rudder asphalt are the follows: 1) The amount of water absorption was '0.06'g and the seepage quality was '0'g in result. 2) The tensile strength was about 30.7kgf/$\textrm{cm}^2 and the elongation was about 72.4% in result. 3) After reliance of temperature test had been ended, the tensile strength was about 72.4kgf/$\textrm{cm}^2 in low temperature and about 30.7kgf/$\textrm{cm}^2 in normal temperature. 4) After acid and alkaline treatment had been ended, the tensile strength was about 19.7kgf/$\textrm{cm}^2$ and about 21.9kgf/$\textrm{cm}^2 in result. 5) After chlorine ion treatment had been ended, the tensile strength was 28.5kgf/$\textrm{cm}^2$ and the elongation was 250% in result. 6) The impact performance was subsided at 1.5m height. 7) After promotion weathering had been ended, the tensile and elongation was about 26.0kgf/$\textrm{cm}^2, 214% in result. So, this study can propose the spray water-soluble rubber asphalt to satisfy the and durability of waste filled land.