Abstract
Eight direct tension tests were conducted to study the bond characteristics and crack behavior in high-strength concrete axial members. The main variable was the concrete strength up to 61-63 MPa. The specimens consisted of two different types of the short specimens modeled the part between transverse cracks and the long specimens having numerous transverse cracks. The results obtained show that the bond strength increases in proportion to compressive strength. Thereby, in high-strength concrete the length of stress-disturbed region is shortened and the space of adjacent transverse cracks become smaller. Although the concrete strength varies from 25 MPa to 61 MPa, the split cracking loads remain constant, while transverse cracking loads vary as variation of concrete tensile strength. Accordingly, the current code provisions for development length may need reconsideration in high-strength concrete members, and it is recommended that either thicker cover or transverse reinforcement should be additionally provided for high-strength concrete members.
본 연구는 8개의 직접인장실험을 수행하여 축방향 부재의 콘크리트강도에 따른 부착특성과 균열거동을 조사하였다. 주변수는 콘크리트강도로 보통강도 24-25 MPa, 고강도 61-63 MPa이다. 직접인장시험체는 2종류로서 짧은 시험체는 횡균열 사이의 인장부재를 모형화하였고, 긴 시험체는 다수의 횡균열이 발생하는 인장부재를 모형화하였다. 이러한 직접인장실험을 수행하여 다음과 같은 결론을 얻었다. 부착강도는 압축강도에 비례하여 증가한다. 그러므로 고강도콘크리트에서 응력교란구간의 길이는 더 짧아지고 횡균열 간격이 더 줄어든다. 콘크리트강도가 25MPa에서 61MPa으로 증가하였지만 쪼갬균열하중은 거의 같게 나타났다. 반면에 횡균열하중은 인장강도에 비례하여 증가하였다. 따라서 고강도콘크리트를 사용할 때에 현행 구조설계기준의 정착길이 산정방법은 재고될 필요가 있고, 피복두께와 순철근간격을 더 크게 하든지 횡보강철근의 의무화하는 것이 현행 기준에 추가되기를 권장한다.