The effects of heat-treatment with magnetic or non-magnetic field on magnetic properties of gas-atomized MPP dust cores subjected to various cooling processes after annealing were investigated. Upon magnetic-field annealing, ac permeability and core loss decreased with the increase of cooling rate, which were attributed to the generation of inhomogeneous internal stress and anomalous eddy current loss, respectively. It was not observed the formation of ordered phase and the related change in magnetic properties at the cooling stage for MPP dust cores. In MPP alloys, magnetic anisotropy was easily induced through the directional order, and permeability and core loss were changed under the conditions of low cooling rate and magnetic annealing.
가스분무법으로 만든 MPP 압분자심을 무자장 및 자장중에서 열처리한 후 냉각속도를 달리할 때 얻어지는 자기적 특성의 변화를 조사하였다. 무자장중에서 열처리시 냉각속도가 증가하면 교류투자율 및 자심손실이 감소하였으며, 이는 각각 빠른 냉각속도에서의 불균일한 내부음력의 발생과 이상 와전류손실의 감소에 기인하는 것으로 해석되었다. 한편 MPP 압분체를 무자장 열처리 후 냉각속도를 달리하여도 Ni-Fe 합금에서 전형적으로 나타나는 규칙상의 형성에 따른 자기적 특성의 변화는 보이지 않았으나, 느린 냉각속도의 조건하에서 자장열처리를 하면 용이하게 구성원자의 방향성 규칙화에 의해 유도자기이방성이 생성되며 상당한 투자율 및 자심손실의 변화가 얻어지는 것으로 관찰되었다.