A Study on the Thermal Stability of $Ll_2$$Al_3$Ti Intermetallic Compounds Fabricated by Mechanical Alloying with Mn additions

기계적 합금화 방법에 의해 제조된 $Ll_2$$Al_3$Ti금속간 화합물의 열적 안정성에 미치는 Mn의 첨가 영향에 관한 연구

  • 최재웅 (한양대학교 공과대학 재료공학부) ;
  • 박종범 (한양대학교 공과대학 재료공학부) ;
  • 강성군 (한양대학교 공과대학 재료공학부)
  • Published : 2001.05.01
Download PDF
⟨ Previous Next ⟩

Abstract

Fer the purpose of improving ductility of $Al_3$Ti intermetallic compound has potential to industrial application, we investigated formation behavior of cubic Ll$_2$ structure and effect of Mn addition. Nanocrystalline cubic Ll$_2$Al$_3$Ti intermetallic compound, has 10nm size of grain, was fabricated by mechanical alloying for 20hr at the composition of Al-8Mn-25Ti. Ternary cubic Ll$_2$Al$_3$Ti, added Mn, did not showed phase transformation from Ll$_2$ to D0$_{23}$ or D0$_{22}$ unlike binary cubic Ll$_2$Al$_3$Ti and maintained Ll$_2$ structure.

고온구조용 재료로의 사용이 기대되는 $Al_3$Ti금속간 화합물의 연성 향상을 위한 목적으로 기계적 합금화를 통한 cubic Ll$_2$구조의 생성거동과 Mn의 첨가 영향을 조사하였다. Al-8Mn-25Ti조성에서 20시간의 기계적 합금화를 통해 약 1.0nm 사이즈의 grain을 갖는 nanocrystalline cubic Ll$_2$Al$_3$Ti 금속간 화합물이 제조되었다. Mn이 첨가된 3원계 cubic Ll$_2$Al$_3$Ti 금속간 화합물은 2원계 cubic Ll$_2$Al$_3$Ti 금속간 화합물에서 보이는 Ll$_2$구조에서 D0$_{23}$구조나 D0$_{22}$구조로의 상변태가 발생하지 않았으며 Mn의 첨가로 인해 Ll$_2$구조는 120$0^{\circ}C$가지 안정함을 보였다.

Keywords

References

  1. K. S. Kumer and J. R. Pickens, 'Dispersion Strengthened Aluminum Alloys,' edited by Y. M. Kim and Y. H. Griffith, 763 (1988)
  2. J. Tarnacki and Young-Won Kim, 'Dispersion Strengthened Aluminum Alloys,' edited by Y. M. Kim and Y. H. Griffith, 741 (1988)
  3. M. Yamaguchi, Y. Umakoshi, Prog. Mater. Sci, 34, 1 (1990) https://doi.org/10.1016/0079-6425(90)90002-Q
  4. A. Raman and K. Schbert, Z. Metallkde., 56, 99 (1965)
  5. A. Seibold, Z. Metallkd., 72, 712 (1981)
  6. K. S. Kumar and J. R. Pickens, Scr. Metall., 22, 1015 (1988) https://doi.org/10.1016/S0036-9748(88)80094-2
  7. S. Zhang, J. P. Nic, D. E. Mikkola, Scr. Metall., 24, 57 (1990) https://doi.org/10.1016/0956-716X(90)90566-Y
  8. H. Mabuchi, K. Hirukawa and Y. Nakayama, Scr. Metall., 23,1761 (1981) https://doi.org/10.1016/0036-9748(89)90357-8
  9. M. Yamaguchi, H. Inui, Intermetallic Compounds, John Wiley & Sons Ltd, 2, 147 (1994)
  10. M. Kogachi and A. Kameyarna, Scr. Metall., 29, 1329 (1993) https://doi.org/10.1016/0956-716X(93)90133-D
  11. B.D.Cullity, 'Elements of X-ray Diffraction,' A ddison- Wesley Publishing Company, 2nd edition, 101 (1978)
  12. F. Zhang, L. Lu, M.O. Lai, J. Alloys Compd., 297 (2000)