Abstract
Adsorption behaviors of Ni(II) ions were investigated using amorphous alumina as adsorbent. In the adsorption kinetic study, it was observed that Ni(II) ions were bound to the alumina surface in two adsorption stages, the rapid and slow adsorption stages. The rapid adsorption proceeded within 1 hr, thereafter the slow adsorption occurred. The results of adsorption isotherm experiments showed that the Ni(II) adsorption obeyed the Langmuir-Freundlich isotherm, and that the adsorption enhanced with increasing pH. The change in ionic strength did not exhibit a conspicuous trend in Ni(II) adsorption, thereby suggesting that the adsorption occurs through surface complexation rather than electrostatic interactions. The amounts of adsorption were measured with varying pH at three different Ni(II) concentrations under the condition of constant ionic strength, showing that with increasing Ni(II) concentration, the percentage of adsorption decreased and the adsorption edge was shifted to a higher pH value.
무정형 알루미나를 흡착제로 사용하여 니켈(II) 이온의 흡착거동을 조사하였다. 흡착반응속도에 관하여 실험한 결과, 두 단계 흡착, 즉 한 시간 이내 빠르게 진행되는 흡착과 그 이후에는 느리게 진행되는 흡착으로 구분되었다. 흡착등은 실험에서는 Langmuir-Freundlich 흡착식을 만족하였으며 PH가 높을수록 최대흡착량이 증가함을 보였다. 이온강도의 변화에 따른 흡착량의 변화를 조사한 결과 어떤 뚜렷한 경향성을 보이지 않은 것으로 보아 니켈(II) 이온의 흡착은 정전기적 상호작용이라기 보다는 표면착물형성으로 이루어짐을 추정할 수 있었다. 일정한 이온강도에서 세 가지의 니켈(II) 이온 농도에서 pH를 변화시키면서 흡착량을 측정한 결과 니켈(II) 이온의 농도가 높을수록 흡착률은 감소했으며 흡착변곡점은 보다 높은 pH쪽으로 이동하였다.