Abstract
Poly(ethylene glycol) with number-average molecular weight (M$_{n}$) of 200 (PEG 200) or 400 (PEG 400) was reacted with various linking agents (CH$_2$Cl$_2$, CH$_2$Br$_2$, CH$_2$I$_2$, Br(CH$_2$)$_3$Br) in the presence of alkali to form of oxyalkylene linked chains. Molecular weights of copolymers were controlled using feed mole ratio of alkali/CH$_2$C1$_2$/PEG. The M$_{n}$ of the polymers measured by end group analysis and that measured by GPC agreed well. Molecuglar weights of polyether copolymers obtained from PEG 200 and PEG 400 were about 500~8500 and 1000~2000, respectively. Polyether copolymers prepared from PEG 400 showed melting points of around 1$0^{\circ}C$. Glass transition temperatures of the copolymers were around -75$^{\circ}C$ and the crystallinity was about 0~25%. The polyether copolymers prepared from PEG 200 had no crystallinity below the M$_{n}$ of 2500. 2500.
분자량이 200 또는 400인 poly(ethylene glycol) (PEG 200, PEG 400)을 알칼리 존재하에서 다양한 linking agent (CH$_2$C1$_2$, CH$_2$Br$_2$, CH$_2$I$_2$, Br(CH$_2$)$_3$Br)와 반응시켜 oxyalkylene-linked poly(oxyethylene) 공중합체를 합성하였다. 얻어진 공중합체의 분자량은 alkali/CH$_2$C1$_2$/PEG의 당량비를 달리하여 조절하였으며 PEG 200을 사용하였을 경우 약 500~8500, 그리고 PEG 400을 사용하였을 경우 약 1000~2000정도이었다. 말단의 -OH기 농도 적정에 의한 분자량과 GPC에 의해 얻어진 분자량은 서로 거의 일치하였다. PEG 400으로부터 얻어진 공중합체는 유리전이온도가 약 -75$^{\circ}C$정도였고, 용융온도가 1$0^{\circ}C$정도였으며 결정화도가 0~25% 정도이었다. 또한 PEG 200을 이용하여 합성된 공중합체의 경우는 분자량이 2500이하에서는 완전한 비정형 물질임을 알 수 있었다.