Pseudo Liquid Crystallinity and Characteristics of PHB/PEN/PET Melt Blend

PHB/PEN/PET 삼상계 용융혼합물의 의사액정상 및 특성연구

  • 박재기 (한국생산기술연구원 연구기획본부) ;
  • 정봉재 (한양대학교 섬유고분자공학과 기능성고분자신소재 연구센타) ;
  • 김성훈 (한양대학교 섬유고분자공학과 기능성고분자신소재 연구센타)
  • Published : 2000.01.01

Abstract

Poly(p-hydroxybenzoate) (PHB)/poly(ethylene terephthalate) (PET) 8/2 thermotropic liquid crystalline copolyester, poly(ethylene 2,6-naphthalate) (PEN) and PET were mechanically blended to obtain the pseudo liquid crystalline (LC) phase of ternary blends. The torque values of blends with increasing PHB content were abruptly decreased above 40 wt% of PHB content, because the melt viscosity of ternary blends decreased. Tensile strength and initial modulus of blends containing above 30 wt% PHB were improved with increasing PHB content. Tensile strength and modulus of fiber were increased with PHB contents and take-up speed. Degree of transesterification and randomness of blends were increased with blending time. The blend of 40 wt% PHB was shown pseudo LC phase in the polarized optical photographs. Crystallinity of PHB/PEN/PET ternary blend were increased with PHB content.

Poly(p-hydroxybenzoate) (PHB)/poly(ethylene terephthalate) (PET) 8/2공중합 폴리에스테르계 액정고분자와 poly(ethylene 2,6-naphthalate) (PEN) 및 poly(ethylene terephthalate)를 용융혼합하여 삼상계 블렌드물의 액정상 형성여부 및 기계적 성질을 조사하였다. PHB의 함량이 40 mo1%에서 급격한 점도의 감소로 토크의 값이 감소하였고, 인장강도와 초기 탄성율은 PHB의 함량이 증가함에 따라 액정고분자의 피브릴 형성으로 증가하였다. 섬유의 인장강도와 탄성율은 PHB의 함량과 권취속도를 증가시킴에 따라 증가하였고, 에스테르 교환반응은 용융혼합 시간에 따라 증가하였다. 에스테르 교환반응은 용융흔합물의 흔화성을 향상시키고, 동일 조성비의 단량체를 함유한 공중합체에서 나타나는 액정상을 형성하였다. PHB의 함량이 30 wt%에서는 부분적인 액정상이 나타나며, 40 wt%에서 삼상계 블렌드의 의사액정상이 나타났다.

Keywords

References

  1. Brit. Patent 604073 J. G. Cook;H. P. W. Hugill;A. R. Lowe
  2. Polymer v.30 S. Buchner;D. Wiswe;H. G. Zachmann
  3. Polym. Eng. Sci. v.30 no.12 M. Cakmak;Y. D. Wang;M. Simhambhatla
  4. J. Appl. Polym. Sci. v.46 M. Ito;K. Honda;T. Kanamoto
  5. J. Appl. Polym. Sci. v.57 J. Jager;J. A. Juijn;C. J. M. Van Den Heuvel;R. A. Huijts
  6. Polymer v.35 no.26 Y. Ulcer;M. Cakmak
  7. Polymer v.34 no.4 W. C. Lee;A. T. Dibenedetto
  8. J. Appl. Polym. Sci. v.60 H. C. Chin;K. C. Chiou;F. C. Chang
  9. J. Appl. Polym. Sci. v.70 S. H. Kim;S. W. Kang;J. K. Park;Y. H. Park
  10. Korea Patent, Application No.18653 S. H. Kim;S. W. Kang
  11. J. Appl. Polym. Sci. v.74 S. H. Kim;H. O. Yoo;S. M. Hong;S. S. Hwang
  12. J. Appl. Polym. Sci. v.62 K. Yoshikai;K. Nakayama;M. Kyotani
  13. J. Appl. Polym. Sci. v.67 no.8 S. H. Kim;S. W. Park;E. S. Gil
  14. Polymer v.32 no.9 D. Chen;H. G. Zachmann
  15. Polymer v.32 no.12 F. J. Balta-Calleja;C. Santa-Cruz;D. Chen;H. G. Zachmann
  16. Polymer v.35 no.18 S. Spies;H. G. Zachmann
  17. Macromolecules v.29 no.14 O. Ahumada;T. A. Ezquerra;A. Nogales;F. J. Balta-Calleja;H. G. Zachmann
  18. SAMPE J. v.6 no.6 J. Economy;B. E. Nowak;S. G. Cottis
  19. J. Appl. Polym. Sci. Ed. v.5 R. Yamadera;M. Murano