Abstract
The considerations for remaining life of ACSR (Aluminum Stranded Conductors Steel Reinforced) in transmission lines have become gradually important to hold reliability and stability of power supply. The remaining life of ACSR exposed to the atmosphere for a long period may rely on deterioration caused by environmental indices such as atmospheric corrosion, galvanic corrosion, crevice corrosion and fatigue corrosion. One of reduction of useful life in overhead transmission lines built on the ridge of mountain is often caused by forest fires.This paper deals with investigation of strength deterioration performance of ASCR due to fires through several testing and analyzing data for tension load and extension of blazed ACSR. Test samples are ACSR 480[$\textrm{mm}^2$] conductors, which are artificially fired to regular durations. Mechanical properties such as tension load and extension for fired ACSR conductors are tested and estimation functions for mechanical performances corresponding to fire duration are determined. As a result, it can be verified that both tension load and extension of ACSR are reduced by increasing fire duration. Hence, it is obvious that ACSR due to forest fires may lead to mechanical deterioration.
송전선로의 ACSR(Aluminum Strandard Conductors Steel Reinforced)의 잔존수명에 대한 관심이 전력공급의 신뢰성과 안정성올 유지하기 위하여 점차 중요하게 되있다. 대기 중에 장기간 노출된 ACSR의 잔존수명은 대기부식, 전해부식, 간극부식과 피로부식과 같은 환경요인들에 의하여 발생된 열화에 의존된다. 산 등성이에 가설된 가공 송전선에 유효수명의 감소 중 하나는 종종 산불에 의한 것이다. 이 논문에서는 화염에 노출된 ACSR의 인장하중과 연신율에 대한 몇 가지 시험과 해석 결과를 통하여 화염에 의한 ACSR의 기체적 열화특성 고찰한다 시힘 시료는 ACSR 480[ml] 도체들로, 일정한 시간간격으로 인공적으 로 가열된 것들이다. 가열된 ACSR 도체를에 대한 인장하중과 연산율과 같은 기계적 특성이 시험되고 가열시간에 의한 기계적 특성의 추정함수들미 결정되었다. 그 결과, ACSR의 인장하증과 연신율 모두가 가열시간이 증가함에 따라 감소되는 것 확인할 수 있었다. 따라서, ACSR은 산블에 의하여 기계적인 멸화가 진전될 것이 분명하다.