Effect of Coatings of Oxidized Starch on Properties of Linerboard

산화전분 코팅이 골판지 원지의 물성에 미치는 영향

Two linerboards consisting of corrugated board were coated with oxidized starch solutions to investigate the change of their properties and analyze the effect of coating on them. The coating of linerboards with oxidized starch resulted in improvement in the properties related to corrugated board properties by increasing fiber bonding and rigidity. The improvement of ring crush strength by coating was greater in inside linerboard than in outside linerboard. Burst index of linerboards rapidly increased with an initial increase of coating weight, but as the coating weight further increased, there was no increase in burst index. Coating on linerboards with oxidized starch at low coating weight improved stiffness of them. There were no significant changes in tearing resistance of linerboards by coating of oxidized starch. The coating resulted in increase in air resistance and sizing degree of linerboards.

산화전분을 골판지 구성원지인 표면라이너지와 이면라이너지에 각각 코팅하고 물성변화를 조사하였다. 산화전분 코팅에 의해 골판지 믈성과 관련된 각 라이너지의 물성이 개선되었고 링 크러시 강도의 경우 표면라이너지보다 이면라이너지에서 개선의 효과가 더욱 컸으며 도공하지 않은 경우에 비해 최대 19.7%의 증가를 보였다. 비교적 낮은 도공량으로도 파열지수는 증가하였으며 일정 수준의 도공량 이상에서는 더 이상 증가하지 않는 것으로 조사되었다. 파열강도가 증가함에 따라 링 크러시 강도도 증가하는 경향을 보였다. 표면라이너지, 이면라이너지 각각 1.41g/$m^2$, 1.58g/$m^2$의 도공량에 이를 때까지 TEA는 크게 증가하였으며 인장강도가 증가함에 따라 링 크러시 강도도 대체적으로 증가되었다. 낮은 도공량에서 stiffness가 증가하였으며 도공처리로 라이너지의 투기도는 감소하였지만 원지 간 결합에 장애를 일으킬 만큼의 염려는 없을 것으로 판단되었다.