Composition and Microstructure of Punch'ong Sherds from Bokwang-ri, Kangnung

강릉 보광리 분청도편의 성분과 미세구조 연구

  • Kim, Kyung-nam (Department of Materials Engineering, Samchok National University) ;
  • Han, Sang-mok (Department of Advanced Materials Engineering, Kangwon National University) ;
  • Shin, Dae-yong (CACP, Kangwon National University)
  • 김경남 (삼척대학교 재료공학과) ;
  • 한상목 (강원대학교 신소재공학과) ;
  • 신대용 (강원대학교, 석재복합신소재연구센터)
  • Published : 1999.12.01
Download PDF
⟨ Previous Next ⟩

Abstract

The chemical compositions and microstructure of the punch'ong excavated from Bokwangri, Kangnung were investigated by the scanning electron microscope (SEM) with an energy dispersive X-ray spectrometer (EDS), X-ray diffractometer (XRD), and dilatometer. The compositions of body were $SiO_2(73-78\%),\;Al_2O_3(13-16\%)$, $RO{\cdot}R_2O(4-5\%,\;R=Ca,\;Mg,\;Na,\;K),\;R_xO_y(3-6\%,\;R=Fe,Ti)$ in weight ratio, which were higher silica and flux $(RO{\cdot}R_2O)$ but lower alumina. Owing to the high content$(21-30\%)$ of calcium oxide the glaze is considered lime type. Firing temperature range for the ceramic was presumed to about $1150^{\circ}C$.

강릉 보광리 도요지에서 출토된 분청 도편의 성분과 미세구조의 특징을 EDS부착의 주사전자현미경과 X선 회절분석기, 열팽창측정기를 이용하여 조사하였다. 도편의 태토 성분은 $SiO_2(73-78\%),\;Al_2O_3(13-16\%)$, $RO{\cdot}R_2O(4-5\%,\;R=Ca,\;Mg,\;Na,\;K),\;R_xO_y(3-6\%,\;R=Fe,Ti)$로 구성되어 있으며, $SiO_2$의 양은 많은 편이나 $Al_2O_3$의 양은 적은 편이었다. 유약은 CaO 함량이 $21-30\%$로 높은 것으로 보아 석회계열의 유약으로 생각된다. 또한 도편의 소성온도는 $1150^{\circ}C$부근의 온도로 추정된다.