THE EFFECTS OF THERMOCONDENSATION TECHNIQUE USING SYSTEM B^TM ON THE PERIODONTIUM

System B^TM를 이용한 열가압 충전시의 치주인대내에 미치는 영향

Thermocondensation root canal filling technique have been used to fill accessary canals or to obtain homogeneous root caral fillings. But these thermocondensation technique inevitably produce heat in the canal which can be transmitted through the dentin and cementum and consequently damage periodontal ligamental cells and osteoblasts. In this study, System $B^{TM}$(Analytic technology, WA.D.S.A.) was used to evaluate the reaction of periodontal ligament tissue to "Continous Wave condensation technique" introduced by Buchanan, and the transmitted root surface temperature was measured according to measured root thicknesses. 12 Mandibular incisors of two adult dogs were used for the experiment. 6 controls were filled by lateral condensation technique with sealer.3 specimens were apically filled by Continuous Wave technique at $200^{\circ}C$ for 5 seconds and remaining 3 specimens were additionally backfilled using System $B^{TM}$(Analytic technology, WA.D.S.A.) was used to evaluate the reaction of periodontal ligament tissue to "Continous Wave condensation technique" introduced by Buchanan, and the transmitted root surface temperature was measured according to measured root thicknesses. 12 Mandibular incisors of two adult dogs were used for the experiment. 6 controls were filled by lateral condensation technique with sealer.3 specimens were apically filled by Continuous Wave technique at $200^{\circ}C$ for 5 seconds and remaining 3 specimens were additionally backfilled using System $B^{TM}$ at $100^{\circ}C$ for 20 seconds. Six weeks later, the dogs were sacrificed and the teeth stained with Hematoxylin and Eosin for histologic examination. 6 extracted human teeth were used to measure the transmitted temperature. After cutting off the crown, the canals were prepared and divided into 3 groups with root thickness of 1.5mm, 1.0mm, 0.5mm, 2 teeth in each group. Inside each root canal, System $B^{TM}$ was heated as with the temperature for the apically condensed and the back filled group, and the transmitted heat was measured on the external surface of the root. The temperature of System $B^{TM}$ heat spreader at $200^{\circ}C$ and $100^{\circ}C$ was also measured at root temperature. It can be concluded as follows: 1. In the thin area (200-$250{\mu}m$) of the root, root resorption could be seen even with heating at $200^{\circ}C$ for 5 seconds. 2. When the spreader was heated at $200^{\circ}C$ for 5 seconds and additionally at $100^{\circ}C$ for 20 seconds for backfill, all teeth showed root resorption regardless of their root thickness. 3. The transmitted external root surface temperature was higher as the root thickness decreased and as the heating time increased. In the thermocompaction technique using System $B^{TM}$, the spreader should be heated for the minimal time and used only in the apical area. The heated spreader shouldn't inserted to the binding point of the canal and backfilling should be done with other means of minimally heated gutta percha technique.