Abstract
High quality diamond films of the silicon on diamond (SOD) structure are deposited using CO and $H_2$ gas mixture in microwave plasma chemical vapor deposition (CVD), a SOD structure is fabricated using low pressure CVD polysilicon on diamond/ Si(100) substrate. The crystalline structure of the diamond films which composed of { 111} and {100} planes. were changed from octahedral one to cubo-octahedron one as the CO/$H_2$ ratios are increased. The high quality diamond films without amorphous carbon and non-diamond elements were deposited at the CO/$H_2$ flow rate of 0.18. and the main phase of the diamond films shows (111) plane. The diamond/Si(lOO) structure shows that the interface is flat without voids. The measured dielectric constant. leakage current and breakdown field were $5.31\times10^{-9}A/cm^2$ and $9\times{10^7}{\Omega}cm$ respectively.
CO와 $H_2$의 탄소원을 사용한 마이크로파 플라즈마 화학기상증착 방법으로 SOD 구조에 적용될 양질의 다이아몬드 박막을 형성하였고, SOD 구조를 형성하기 위해 diamond/Si(100) 구조 위에 poly-Si 박막을 저압화학기상 증착법으로 제작하였다. CO/$H_2$탄소원의 유량비 증가에 따라 다이아몬드의 결정은 octahedron 구조에서 cubo-octahedron 구조로 바뀌었으며, 결정면은 {111}과 {100}으로 혼합되어 형성되었다. 비정질 carbon과 non-diamond성분이 없는 양질의 다이아몬드 박막은 CO/$H_2$의 유량비가 0.18일 때 형성되었으며, 주 결정상은 (111) 면이었다. diamond/Si(100) 계면은 void가 없는 평활한 계면을 이루었으며, 다이아몬드 박막의 유전상수, 누설전류와 비저항은 각각 $5.31\times10^{-9}A/cm^2$ 그리고 $9\times{10^7}{\Omega}cm$이었다.