Abstract
The fluorine doped silicon oxide (SiOF) intermetal dielectric (IMD) films have been of interest due to their lower dielectric constant and compatibility with existing process tools. However instability issues related to bond and increasing dielectric constant to water absorption when the SiOF films was exposured to atmospheric ambient. Therefore, the purpose of this research is to study the effect of post oxygen plasma treatment on the resistance of moisture absorption and reliability of SiOF film. Improvement of moisture absorption resistance of SiOF film is due to the forming of thin SiO₂layer at the SiOF film surface. It is thought that the main effect of the improvement of moisture absorption resistance was densification of the top layer and reduction in the number of Si-F bonds that tend to associate with OH bonds. However, the dielectric constant was increased when plasma treatment time is above 5 min. In this study, therefore, it is thought that the proper plasma treatment time is 3 min when plasma treatment condition is 700 W of microwave power, 3 mTorr of process pressure and 300℃ of substrate temperature.
ECR plasma CVD를 이용한 SiOF박막은 낮은 유전상수를 가지고 있으며, 기존의 공정과의 정합성이 우수해 다층배선 공정에 채용이 유망한 재료이지만 수분의 흡수로 인한 유전율의 상승과 후속공정의 안정성이 문제점으로 부각되고 있다. 따라서 본 연구에서는 SiOF박막의 내흡습성과 후속공정에서의 안정성을 향상시키기 위하여 SiOF박막을 증착한 후 후속 산소 플라즈마 처리를 행하였다. SiOF박막은 산소 플라즈마 처리를 수행함으로써 SiOF박막의 밀도가 증가하고, 수분과의 친화력이 강한 Si-F 결합이 감소하는 것이 주요한 원인으로 사료된다. 하지만 플라즈마 처리 시간이 5분 이상으로 증가하면 유전율의 증가가 일어난다. 따라서 본 실험에서는 산소 플라즈마 처리조건이 마이크로파 전력이 700W, 공정 압력이 3mTorr, 기판온도가 300℃일 경우 플라즈마 처리시간은 3분이 적당한 것으로 생각 된다.봉？향상시키기 위하여 SiOF박막을 증착한 후 후속 산소 플라즈마 처리를 행하였다. SiOF박막은 산소 플라즈마 처리를 수행함으로써 SiOF박막의 밀도가 증가하고, 수분과의 친화력이 강한 Si-F 결합이 감소하는 것이 주요한 원인으로 사료된다. 하지만 플라즈마 처리 시간이 5분 이상으로 증가하면 유전율의 증가가 일어난다. 따라서 본 실험에서는 산소 플라즈마 처리조건이 마이크로파 전력이 700W, 공정 압력이 3mTorr, 기판온도가 300℃일 경우 플라즈마 처리시간은 3분이 적당한 것으로 생각된다.